NORSODYNE® M 01070
- Chemical Family
- Unsaturated Polyester (UPE)
NORSODYNE® M 01070 - Pure maleic unsaturated polyester resin in styrene. It is used to produce bmc and smc manufacture,very good mechanical properties through hot press molding,injection molding,rtm method.
Product families
Applications
Applications
- Consumer Goods — Appliances & Electronics
Automotive & Transportation — Automotive
- Chassis & Brake
- Exterior & Body
- Interior
- Powertrain & UTH
Industrial — Chemical & Industrial Manufacturing
- Equipment & Parts
Industrial — Oil, Gas & Mining
- Refining & Gas Processing
Electrical & Electronics — Parts & Components
- Housings & Enclosures
- Printed Circuit Boards (PCBs)
Industrial — Power, Water & Utilities
- Power & Utilities
- Renewable Energy
Automotive & Transportation — Transportation
- Aerospace & Aviation
- Marine
- Rail & Mass Transit
Product Families
Composite Materials — Polymers & Resins
- Thermoset Resins
Other characteristics
- Brand
- NORSODYNE
- End Uses
- Pipes, Tanks
- Polymer Name
- Polyester (unspecified)
- Processing Methods
Compression Molding, Resin Transfer Molding (RTM)
- Markets
- Automotive & Transportation
- Consumer Goods
- Electrical & Electronics
- Industrial
- Shelf LIfe
- 9 Months (23°C in Dark )
- Technology
- Composite Materials
- Composites End Use
- Pipes
- Tanks
- HIGHLIGHTS
- Good compatibility with thermoplastic additives
- Good pigmentability
- Thickenable with MgO
- Handling
Store in the shade, out of direct sunlight; Keep storage temperature below 25°C; Unseal container just before use; Shelf life will be reduced reaching higher temperature
- Composite Materials Functions
- Resins Binders & Matrix Materials
- Composites Processing Methods
- Compression Molding
- Resin Transfer Molding (RTM)
Technical data
Table 1 of 2
6 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Specific weight at 20°C | 1,10 | g/cm3 | — |
| Brookfield Viscosity at 23°C, sp 2 rpm 10 | 1400 - 1600 | mPa.s | MT-CU023V |
| Solid Content | 66 - 69 | % | MT-CU001C |
| Gel Time at 130°C + 1% TBPB | 55 - 75 | sec | MT-CU003R |
| Delta at 130°C + 1% TBPB | 1:30 - 2:00 | minutes | MT-CU003R |
| Exothermic peak at 130°C + 1% TBPB | 265 - 285 | °C | MT-CU003R |
Table 2 of 2
6 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Elongation at break at 80°C for 16h / +2h at 140°C | 1,3 | % | ISO 527 (2012) |
| Tensile strength at 80°C for 16h / +2h at 140°C | 35 | MPa | ISO 527 (2012) |
| Tensile Modulus at 80°C for 16h / +2h at 140°C | 3165 | MPa | ISO 527 (2012) |
| Flexural strength at 80°C for 16h / +2h at 140°C | 90 | MPa | ISO 178 (2011) |
| Flexural modulus at 80°C for 16h / +2h at 140°C | 3150 | MPa | ISO 178 (2011) |
| HDT at 80°C for 16h / +2h at 140°C | 147 | °C | ISO 75 -2A (2013) |