To catalogue
ENYDYNE® H 66126 TAE
ENYDYNE® H 66126 TAE - Unsaturated polyester resin in styrene,DCPD. It is used to produce pipes and tanks through hand lay up and spray up method.
Product families
Applications
Building & Construction — Building Envelope & Roofing
- Glazing & Window Elements
- Shingles & Tiles
Building & Construction — Building Materials
- Fence Decks & Rails
- Interior Fixtures
- Pipes & Plumbing
- Siding & Trim
- Structural Components
- Wall Panels
Industrial — Chemical & Industrial Manufacturing
- Equipment & Parts
Building & Construction — Infrastructure, Roads & Paving
- Pavement Highways Roads & Bridges
Industrial — Oil, Gas & Mining
- Refining & Gas Processing
Industrial — Power, Water & Utilities
- Power & Utilities
- Renewable Energy
Product Families
Composite Materials — Polymers & Resins
- Thermoset Resins
Other characteristics
- Brand
- ENYDYNE
- End Uses
- Pipes, Tanks
- Polymer Name
- Polyester (unspecified)
- Processing Methods
- Hand Lay-up, Spray Lay-up
- Markets
- Building & Construction
- Industrial
- Shelf LIfe
- 6 Months (23°C in Dark )
- Technology
- Composite Materials
- Product Safety
Stir the resin before use, without use air bubbles, As the resin includes a film-forming agent, we recommend that the laminate should first rubbed down before bonding or relaminating.
- Application Methods
- Spray
- Composites End Use
- Pipes
- Tanks
- HIGHLIGHTS
- Low styrene emission
- Preaccelerated
- Medium reactivity
- Thixotropic
- Handling
Store in the shade, out of direct sunlight; Keep storage temperature below 25°C; Unseal container just before use; Shelf life will be reduced reaching higher temperature
- Composite Materials Functions
- Resins Binders & Matrix Materials
- Composites Processing Methods
- Hand Lay-up
- Spray Lay-up
Technical data
Table 1 of 2
6 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Solid Content | 57 - 61 | % | MT-CU001C |
| Specific weight at 20°C | 1,10 | g/cm3 | — |
| Brookfield Viscosity at 23°C, sp 2 rpm 50 | 350 - 750 | mPa.s | MT-CUT23V |
| Gel Time at 23°C + 1,5% MEKP50 | 10-12 | minutes | MT-CU151R |
| Peak at 23°C + 1,5% MEKP50 | 15 - 20 | minutes | MT-CU151R |
| Exothermic peak at 23°C + 1,5% MEKP50 | 120 - 140 | °C | MT-CU151R |
Table 2 of 2
6 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile strength at 140°C for 16h /+ 2 h at 90°C | 45 | MPa | ISO 527 (2012) |
| Tensile Modulus at 140°C for 16h /+ 2 h at 90°C | 3550 | MPa | ISO 527 (2012) |
| Flexural strength at 140°C for 16h /+ 2 h at 90°C | 90 | MPa | ISO 178 (2011) |
| Flexural modulus at 140°C for 16h /+ 2 h at 90°C | 3500 | MPa | ISO 178 (2011) |
| HDT at 140°C for 16h /+ 2 h at 90°C | 65 | °C | ISO 75 -2A (2013) |
| Elongation at break at 140°C for 16h /+ 2 h at 90°C | 1,55 | % | ISO 527 (2012) |