NORSODYNE® R 56372 TAE
NORSODYNE® R 56372 TAE - Unsaturated polyester resin in styrene,Isophthalic-Neopentylic. It is used to produce relining,cipp,pipes and tanks through continuous laminating method.
Product families
Applications
Building & Construction — Building Envelope & Roofing
- Glazing & Window Elements
- Shingles & Tiles
Building & Construction — Building Materials
- Fence Decks & Rails
- Interior Fixtures
- Pipes & Plumbing
- Siding & Trim
- Structural Components
- Wall Panels
Industrial — Chemical & Industrial Manufacturing
- Equipment & Parts
Building & Construction — Infrastructure, Roads & Paving
- Pavement Highways Roads & Bridges
Industrial — Oil, Gas & Mining
- Refining & Gas Processing
Industrial — Power, Water & Utilities
- Power & Utilities
- Renewable Energy
Product Families
Composite Materials — Polymers & Resins
- Thermoset Resins
Other characteristics
- Brand
- NORSODYNE
- End Uses
- Pipes, Structural Components, Tanks
- Polymer Name
- Polyester (unspecified)
- Processing Methods
- Continuous Lamination
- Markets
- Building & Construction
- Industrial
- Shelf LIfe
- 6 Months (23°C in Dark )
- Technology
- Composite Materials
- Product Safety
Stir the resin before use, without use air bubbles, As the resin includes a film-forming agent, we recommend that the laminate should first rubbed down before bonding or relaminating.
- Composites End Use
- Pipes
- Structural Components
- Tanks
- Material Features
- Chemical Resistant
- HIGHLIGHTS
- Low styrene emission
- Preaccelerated
- Thixotropic
- Very good chemical resistance
- Handling
Store in the shade, out of direct sunlight; Keep storage temperature below 25°C; Unseal container just before use; Shelf life will be reduced reaching higher temperature
- Composite Materials Functions
- Resins Binders & Matrix Materials
- Composites Processing Methods
- Continuous Lamination
Technical data
Table 1 of 2
6 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Solid Content | 58 - 62 | % | MT-CU001C |
| Specific weight at 20°C | 1,12 | g/cm3 | — |
| Brookfield Viscosity at 25°C, sp 3 rpm 50 | 800 - 1000 | mPa.s | MT-CUT25V |
| Gel Time at 60°C + peroxydes | 20 - 30 | minutes | MT-CU149R |
| Curing Time at 60°C + peroxydes | 23 - 35 | minutes | MT-CU149R |
| Exothermic peak at 60°C + peroxydes | 180 - 220 | °C | MT-CU149R |
Table 2 of 2
6 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile strength at 40°C for 16h /+ 2 h at 90°C | 70 | MPa | ISO 527 (2012) |
| Elongation at break at 40°C for 16h /+ 2 h at 90°C | 3,6 | % | ISO 527 (2012) |
| Tensile Modulus at 40°C for 16h /+ 2 h at 90°C | 3500 | MPa | ISO 527 (2012) |
| Flexural strength at 40°C for 16h /+ 2 h at 90°C | 130 | MPa | ISO 178 (2011) |
| Flexural modulus at 40°C for 16h /+ 2 h at 90°C | 3500 | MPa | ISO 178 (2011) |
| HDT at 40°C for 16h /+ 2 h at 90°C | 100 | °C | ISO 75 -2A (2013) |