DISTITRON® 316 T80

Chemical Family: Polyesters, Unsaturated Polyester (UPE)PolyestersUnsaturated Polyester (UPE)

DISTITRON® 316 T80 - Unsaturated polyester resin in styrene,Orthophthalic. It is used to produce buttons through casting (rods) method.

Product families

Building & Construction — Building Envelope & Roofing

Building & Construction — Building Materials

Building & Construction — Infrastructure, Roads & Paving

Composite Materials — Polymers & Resins

Brand: DISTITRON
Polymer Name: Polyester (unspecified)
Markets: Building & Construction
Shelf LIfe: 3 Months (23°C in Dark )
Technology: Composite Materials
Product Safety: Stir the resin before use, without use air bubbles
HIGHLIGHTS: Clear unaccelerated
Thixotropic
Handling: Store in the shade, out of direct sunlight; Keep storage temperature below 25°C; Unseal container just before use; Shelf life will be reduced reaching higher temperature
Composite Materials Functions: Resins Binders & Matrix Materials

6 rows

Characteristic	Value	Unit	Method
Solid Content	69 - 73	%	MT-CU001C
Brookfield Viscosity at 25°C, sp 3 rpm 20	1900 - 2600	mPa.s	MT-CU025V
Gel Time on 50 g resin at 25°C + 0,3% Co 1% + 1% MEKP50	18 - 22	minutes	RS.08.G
Delta at 25°C + 0,3% Co 1% + 1% MEKP50	28 - 42	minutes	RS.08.G
Exothermic peak at 25°C + 0,3% Co 1% + 1% MEKP50	50 - 70	°C	RS.08.G
Specific weight at 20°C	1,14	g/cm3	—

5 rows

Characteristic	Value	Unit	Method
Tensile strength at 23°C for 24h /+ 2h at 100°C /+ 1h at 100°C	30	MPa	ISO 527 (2012)
Tensile Modulus at 23°C for 24h /+ 2h at 100°C /+ 1h at 100°C	1800	MPa	ISO 527 (2012)
HDT at 23°C for 24h /+ 2h at 100°C /+ 1h at 100°C	35	°C	ISO 75 -2A (2013)
Glass transition at 23°C for 24h /+ 2h at 100°C /+ 1h at 100°C	51	°C	ASTM E 1545 (2011)
Elongation at break at 23°C for 24h /+ 2h at 100°C /+ 1h at 100°C	18,0	%	ISO 527 (2012)