EPOVIA OPTIMUM® EP KRF 1101 TA
EPOVIA OPTIMUM® EP KRF 1101 TA - Bisphenol-A Epoxy Resin based vinyl ester,without styrene. It is used to produce pipes and tanks through continuous laminating method.
Identification
Product families
Applications
Building & Construction — Building Envelope & Roofing
- Glazing & Window Elements
- Shingles & Tiles
Building & Construction — Building Materials
- Fence Decks & Rails
- Interior Fixtures
- Pipes & Plumbing
- Siding & Trim
- Structural Components
- Wall Panels
Industrial — Chemical & Industrial Manufacturing
- Equipment & Parts
Building & Construction — Infrastructure, Roads & Paving
- Pavement Highways Roads & Bridges
Industrial — Oil, Gas & Mining
- Refining & Gas Processing
Industrial — Power, Water & Utilities
- Power & Utilities
- Renewable Energy
Product Families
Composite Materials — Polymers & Resins
- Thermoset Resins
Other characteristics
- Brand
- EPOVIA OPTIMUM
- End Uses
- Pipes, Tanks
- Polymer Name
- Vinyl Ester Resin
- Processing Methods
- Continuous Lamination
- Markets
- Building & Construction
- Industrial
- Shelf LIfe
- 6 Months (23°C in Dark )
- Technology
- Composite Materials
- Product Safety
Stir the resin before use, without use air bubbles
- Composites End Use
- Pipes
- Tanks
- Material Features
- Chemical Resistant
- HIGHLIGHTS
- Preaccelerated
- Without styrene in a reactive monomer
- Thixotropic
- Very good chemical resistance
- Handling
Store in the shade, out of direct sunlight; Keep storage temperature below 25°C; Unseal container just before use; Shelf life will be reduced reaching higher temperature
- Composite Materials Functions
- Resins Binders & Matrix Materials
- Composites Processing Methods
- Continuous Lamination
Technical data
Table 1 of 2
6 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Specific weight at 20°C | 1.05 - 1.10 | g/cm3 | — |
| Brookfield Viscosity at 23°C, sp 3 rpm 50 | 800 - 1000 | mPa.s | MT-CUT23V |
| Solid Content | 50 - 55 | % | MT-CU001C |
| Gel Time | 15 - 23 | minutes | MT-CU149R |
| Curing Time | 20 - 30 | minutes | MT-CU149R |
| Exothermic peak | 130 - 140 | °C | MT-CU149R |
Table 2 of 2
8 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Flexural strength | 70 | MPa | ISO 178 (2011) |
| Flexural modulus | 3500 | MPa | ISO 178 (2011) |
| Curing Cycle at 80°C (at 120°C) | 16 (2) | hr | — |
| Tensile strength | 30 | MPa | ISO 527 (1999) |
| Tensile Modulus | 3500 | MPa | ISO 527 (2012) |
| Elongation at break | 0.8 | % | ISO 527 (2012) |
| HDT | 118 | °C | ISO 75 -2A (2013) |
| Barcol Hardness at 25°C | 55 | — | ASTM D 2583 (2007) |