ENYDYNE® I 68871 A
ENYDYNE® I 68871 A - Unsaturated polyester resin in styrene,DCPD. It is mainly used in hand lay up and spray up,injection molding,RTM etc.
Product families
Applications
Building & Construction — Building Envelope & Roofing
- Glazing & Window Elements
- Shingles & Tiles
Building & Construction — Building Materials
- Fence Decks & Rails
- Interior Fixtures
- Pipes & Plumbing
- Siding & Trim
- Structural Components
- Wall Panels
Industrial — Chemical & Industrial Manufacturing
- Equipment & Parts
Building & Construction — Infrastructure, Roads & Paving
- Pavement Highways Roads & Bridges
Industrial — Oil, Gas & Mining
- Refining & Gas Processing
Industrial — Power, Water & Utilities
- Power & Utilities
- Renewable Energy
Automotive & Transportation — Transportation
- Marine
- Rail & Mass Transit
Product Families
Composite Materials — Polymers & Resins
- Thermoset Resins
Other characteristics
- Brand
- ENYDYNE
- End Uses
- Pipes, Tanks
- Polymer Name
- Polyester (unspecified)
- Processing Methods
- Resin Transfer Molding (RTM)
- Color
- Green
- Markets
- Automotive & Transportation
- Building & Construction
- Industrial
- Shelf LIfe
- 6 Months (23°C in Dark )
- Technology
- Composite Materials
- Application Methods
- Spray
- Composites End Use
- Pipes
- Tanks
- Shelf Life Storage
Store in the shade, out of direct sunlight. Keep storage temperature below 25°C. Unseal container just before use. Shelflife will be reduced reaching higher temperature.
- Composite Materials Functions
- Resins Binders & Matrix Materials
- Composites Processing Methods
- Resin Transfer Molding (RTM)
Technical data
Table 1 of 2
7 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Solid Content | 56 - 60 | % | MT-CU001C |
| Specific weight at 20°C | 1,12 | g/cm3 | — |
| Brookfield Viscosity at 23°C, sp 2 rpm 50 | 130 - 170 | mPa.s | MT-CU023V |
| Gel Time | 65 - 85 | minutes | MT-CU151R |
| Exothermic peak | 85 - 105 | °C | MT-CU151R |
| Reactivity at 23°C | + 0,15 DMA + 3 | & | MEKP50 |
| Peak (23°C) | 95 - 115 | — | — |
Table 2 of 2
8 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Flexural strength | 90 | MPa | ISO 178 (2011) |
| Curing Cycle at 23°C (at 100°C) | 24 (1) | hr | — |
| Tensile strength | 53.2 | MPa | ISO 527 (2012) |
| Tensile Modulus | 3720 | MPa | ISO 527 (2012) |
| Elongation at break | 1.7 | % | ISO 527 (2012) |
| Flexural modulus | 3400 | MPa | ISO 178 (2011) |
| HDT | 87 | °C | ISO 75 -2A (2013) |
| Volemetric Shrinkage | 7.2 | % | — |