Polynt Group BMC LPA 240/20
Polynt Group BMC LPA 240/20 Neutro is a bulk molding compound based on an unsaturated polyester resin class “A” grade reinforced with glass fibers. This BMC has been developed for body panel application, with excellent varnish adhesion and excellent surface. BMC LPA 240/20 Neutro is formulated according to RoHS, REAC regulation SVHC and WEEE European legislation.
Product families
Applications
Automotive & Transportation — Transportation
- Rail & Mass Transit
Product Families
Composite Materials — Prepregs & Molding Compounds
- Bulk Molding Compounds (BMC)
Other characteristics
- Functions
- Molding Compound
- Reinforcement Material
- Glass Fibers
- Markets
- Automotive & Transportation
- Technology
- Composite Materials
- Material Features
- Good Surface Appearance
- Handling
Storage in a dry place at 15-25°C, out of direct sun light; Molding time 30 s/mm; Molding pressure 60 - 110 bar; Molding temperature 140 - 160°C
- Certifications and Compliance
- REACH (Europe)
- Composite Materials Functions
- Molding Compound
Technical data
Table 1 of 1
9 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Heat distortion temperature HDT | min. 200 | °C | ISO 75 |
| Quantity of glass | 20 | % | — |
| Hardness Barcol | 50 | — | EN 59 |
| Linear Shrinkage | -0.05 | % | ISO 2577 |
| Flexural strength | 100 | Mpa | ISO 14125A |
| Flexural modulus | 11 | Mpa | ISO 14125A |
| Impact strength (Charpy) | 40 | KJ/m2 | ISO 179 |
| Water absorption | 0,3 | % | ISO 62 Met. 1 |
| Density | 1,9 | g/cm3 | ISO 1183 |