DISTITRON® 183 CAV5F
DISTITRON® 183 CAV5F - Unsaturated polyester resin in styrene,Isophthalic. It is used to produce production of gelcoat through mix with fillers and/or additives.
Product families
Applications
Industrial — Chemical & Industrial Manufacturing
- Equipment & Parts
Industrial — Oil, Gas & Mining
- Refining & Gas Processing
Industrial — Power, Water & Utilities
- Power & Utilities
- Renewable Energy
Product Families
Composite Materials — Polymers & Resins
- Thermoset Resins
Other characteristics
- Brand
- DISTITRON
- End Uses
- Pipes, Tanks
- Polymer Name
- Polyester (unspecified)
- Color
- Yellow
- Markets
- Industrial
- Shelf LIfe
- 3 Months (23°C in Dark )
- Technology
- Composite Materials
- Composites End Use
- Pipes
- Tanks
- HIGHLIGHTS
- Clear unaccelerated
- Handling
Store in the shade, out of direct sunlight; Keep storage temperature below 25°C; Unseal container just before use; Shelf life will be reduced reaching higher temperature
- Composite Materials Functions
- Resins Binders & Matrix Materials
Technical data
Table 1 of 2
7 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Specific weight at 20°C | 1, 11 | g/cm3 | — |
| Solid Content | 60 - 64 | % | MT-CU001C |
| Exothermic peak at 20°C + 1,5% MEKP50 | 185 - 215 | °C | RS.08.G |
| Acidity at 20°C + 1,5% MEKP50 | 11-18 | mg KOH/g | MT-CU001I |
| Brookfield Viscosity at 25°C, sp 2 rpm 20 | 480 - 570 | mPa.s | MT-CUT25V |
| Gel Time at 20°C + 1,5% MEKP50 | 16 - 22 | minutes | RS.08.G |
| Delta at 20°C + 1,5% MEKP50 | 8-14 | minutes | RS.08.G |
Table 2 of 2
7 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Modulus at 23°C for 24h/ + 2h at 100°C /+ 1h at 100°C | 3600 | MPa | ISO 527 (2012) |
| Barcol Hardness at 25°C at 23°C for 24h/ + 2h at 100°C /+ 1h at 100°C | 40 | — | ASTM D 2583 (2007) |
| Tensile strength at 23°C for 24h/ + 2h at 100°C /+ 1h at 100°C | 80 | MPa | ISO 527 (2012) |
| Flexural strength at 23°C for 24h/ + 2h at 100°C /+ 1h at 100°C | 140 | MPa | ISO 178/B (2010) |
| Flexural modulus at 23°C for 24h/ + 2h at 100°C /+ 1h at 100°C | 3500 | MPa | ISO 178/B (2010) |
| HDT at 23°C for 24h/ + 2h at 100°C /+ 1h at 100°C | 80 | °C | ISO 75 -2A (2013) |
| Elongation at break at 23°C for 24h/ + 2h at 100°C /+ 1h at 100°C | 4,2 | % | ISO 527 (2012) |