ENYDYNE® C 66141 L
ENYDYNE® C 66141 L - Unsaturated polyester resin in styrene,DCPD. It is used to produce polymeric concrete through casting method.
Product families
Applications
Building & Construction — Building Envelope & Roofing
- Glazing & Window Elements
- Shingles & Tiles
Building & Construction — Building Materials
- Fence Decks & Rails
- Interior Fixtures
- Pipes & Plumbing
- Siding & Trim
- Structural Components
- Wall Panels
Building & Construction — Infrastructure, Roads & Paving
- Pavement Highways Roads & Bridges
Product Families
Composite Materials — Polymers & Resins
- Thermoset Resins
Other characteristics
- Brand
- ENYDYNE
- Polymer Name
- Polyester (unspecified)
- Markets
- Building & Construction
- Shelf LIfe
- 9 Months (23°C in Dark )
- Technology
- Composite Materials
- Material Features
- Good UV Protection
- HIGHLIGHTS
- Low viscosity
- High reactivity
- Light stabilized
- Handling
Store in the shade, out of direct sunlight; Keep storage temperature below 25°C; Unseal container just before use; Shelf life will be reduced reaching higher temperature
- Composite Materials Functions
- Resins Binders & Matrix Materials
Technical data
Table 1 of 2
6 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Solid Content | 59 - 63 | % | MT-CU001C |
| Specific weight at 20°C | 1,11 | g/cm3 | — |
| Brookfield Viscosity at 23°C, sp 2 rpm 50 | 210 - 250 | mPa.s | MT-CU023V |
| Gel Time at 23°C + 1,2% Co 1% + 1,5% MEKP50 | 3-5 | minutes | MT-CU152R |
| Exothermic peak at 23°C + 1,2% Co 1% + 1,5% MEKP50 | 170 - 190 | °C | MT-CU152R |
| Peak at 23°C + 1,2% Co 1% + 1,5% MEKP50 | 5:30 - 9:30 | — | MT-CU152R min:sec |
Table 2 of 2
6 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile strength at 40°C for 16h / + 2 h at 90°C | 55 | MPa | ISO 527 (2012) |
| Tensile Modulus at 40°C for 16h / + 2 h at 90°C | 3867 | MPa | ISO 527 (2012) |
| Flexural strength at 40°C for 16h / + 2 h at 90°C | 115 | MPa | ISO 178 (2011) |
| Flexural modulus at 40°C for 16h / + 2 h at 90°C | 3800 | MPa | ISO 178 (2011) |
| HDT at 40°C for 16h / + 2 h at 120°C | 74 | °C | ISO 75 -2A (2013) |
| Elongation at break at 40°C for 16h / + 2 h at 90°C | 1,71 | % | ISO 527 (2012) |