To catalogue
DISTITRON® 514 Z1
DISTITRON® 514 Z1 - Unsaturated polyester resin in styrene,Orthophthalic. It is used to produce transparent and corrugated sheets through continuous laminating method.
Product families
Applications
Building & Construction — Building Envelope & Roofing
- Glazing & Window Elements
- Shingles & Tiles
Building & Construction — Building Materials
- Fence Decks & Rails
- Interior Fixtures
- Pipes & Plumbing
- Siding & Trim
- Structural Components
- Wall Panels
Industrial — Chemical & Industrial Manufacturing
- Equipment & Parts
Building & Construction — Infrastructure, Roads & Paving
- Pavement Highways Roads & Bridges
Industrial — Oil, Gas & Mining
- Refining & Gas Processing
Industrial — Power, Water & Utilities
- Power & Utilities
- Renewable Energy
Product Families
Composite Materials — Polymers & Resins
- Thermoset Resins
Other characteristics
- Brand
- DISTITRON
- End Uses
- Pipes, Tanks
- Polymer Name
- Polyester (unspecified)
- Processing Methods
- Continuous Lamination
- Color
- Blue
- Markets
- Building & Construction
- Industrial
- Shelf LIfe
- 3 Months (23°C in Dark )
- Technology
- Composite Materials
- Composites End Use
- Pipes
- Tanks
- Material Features
- Good UV Protection
- HIGHLIGHTS
- Good transparence
- Clear unaccelerated
- Light stabilized
- Handling
Store in the shade, out of direct sunlight; Keep storage temperature below 25°C; Unseal container just before use; Shelf life will be reduced reaching higher temperature
- Composite Materials Functions
- Resins Binders & Matrix Materials
- Composites Processing Methods
- Continuous Lamination
Technical data
Table 1 of 2
7 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Specific weight at 20°C | 1,12 | g/cm3 | — |
| Brookfield Viscosity at 25°C, sp 2 rpm 20 | 200 - 230 | mPa.s | MT-CU025V |
| Solid Content | 58 - 61 | % | MT-CU001C |
| Gel Time at 25°C + 0,2% Co 6% + 1,5%MEKP50 | 5:30 - 5:50 | minutes | RS.08.G |
| Delta at 25°C + 0,2% Co 6% + 1,5%MEKP50 | 7:20 - 8:00 | minutes | RS.08.G |
| Exothermic peak at 25°C + 0,2% Co 6% + 1,5%MEKP50 | 190 - 210 | °C | RS.08.G |
| Acidity at 25°C + 0,2% Co 6% + 1,5%MEKP50 | 24 - 29 | mg KOH/g | MT-CU001I |
Table 2 of 2
8 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Flexural strength at 23°C for 24h/ at 100°C for +2h /at 100°C for +1h | 130 | MPa | ISO 178/B (2010) |
| Tensile strength at 23°C for 24h/ at 100°C for +2h /at 100°C for +1h | 65 | MPa | ISO 527 (2012) |
| Tensile Modulus at 23°C for 24h/ at 100°C for +2h /at 100°C for +1h | 3900 | MPa | ISO 527 (2012) |
| Flexural modulus at 23°C for 24h/ at 100°C for +2h /at 100°C for +1h | 3800 | MPa | ISO 178/B (2010) |
| HDT at 23°C for 24h/ at 100°C for +2h /at 100°C for +1h | 84 | °C | ISO 75 -2A (2013) |
| Glass transition at 23°C for 24h/ at 100°C for +2h /at 100°C for +1h | 103 | °C | ASTM E 1545 (2011) |
| Barcol Hardness at 25°C at 23°C for 24h/ at 100°C for +2h /at 100°C for +1h | 44 | — | ASTM D 2583 (2007) |
| Elongation at break at 23°C for 24h/ at 100°C for +2h /at 100°C for +1h | 2,0 | % | ISO 527 (2012) |