Polynt Group BMC LPA 200/14
Polynt Group BMC LPA 200/14 Neutro is a bulk molding compound based on an unsaturated polyester resin class “A” grade reinforced with glass fibers. This BMC has been developed for reflector of front headlamp automotive. BMC LPA 200/14 Neutro combine an excellent surface, high thermal stability and zero fogging. Excellent varnish adhesion is other peculiarity of BMC LPA 200/14 Neutro. BMC LPA 200/14 Neutro is formulated according to RoHS, REAC regulation SVHC and WEEE European legislation.
Product families
Applications
Automotive & Transportation — Automotive
- Chassis & Brake
- Exterior & Body
- Interior
- Powertrain & UTH
Automotive & Transportation — Transportation
- Aerospace & Aviation
- Marine
- Rail & Mass Transit
Product Families
Composite Materials — Prepregs & Molding Compounds
- Bulk Molding Compounds (BMC)
Other characteristics
- Functions
- Molding Compound
- Reinforcement Material
- Glass Fibers
- Markets
- Automotive & Transportation
- Technology
- Composite Materials
- Material Features
- Good Surface Appearance
- Good Thermal Stability
- Handling
Storage in a dry place at 15-25°C, out of direct sun light; Molding time 30 s/mm; Molding pressure 60 - 110 bar; Molding temperature 140 - 160°C
- Certifications and Compliance
- REACH (Europe)
- Composite Materials Functions
- Molding Compound
Technical data
Table 1 of 1
9 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Heat distortion temperature HDT | min. 200 | °C | ISO 75 |
| Impact strength (Charpy) | 25 | KJ/m2 | ISO 179 |
| Quantity of glass | 14 | % | — |
| Linear Shrinkage | -7 | % | ISO 2577 |
| Flexural strength | 70 | Mpa | ISO 14125A |
| Flexural modulus | 12.5 | Mpa | ISO 14125A |
| Hardness Barcol | 50 | — | EN 59 |
| Water absorption | 0,4 | % | ISO 62 Met. 1 |
| Density | 1,9 | g/cm3 | ISO 1183 |