DISTITRON® 822 S

Chemical Family: Polyesters, Unsaturated Polyester (UPE)PolyestersUnsaturated Polyester (UPE)

DISTITRON® 822 S - Unsaturated polyester resin in styrene,Tetrahydrophthalic. It is used to produce putties through mix with fillers and/or additives.

Product families

Applications

Automotive & Transportation — Automotive

Chassis & Brake
Exterior & Body
Interior
Powertrain & UTH

Industrial — Chemical & Industrial Manufacturing

Equipment & Parts

Industrial — Oil, Gas & Mining

Refining & Gas Processing

Industrial — Power, Water & Utilities

Power & Utilities
Renewable Energy

Automotive & Transportation — Transportation

Aerospace & Aviation
Marine
Rail & Mass Transit

Product Families

Composite Materials — Polymers & Resins

Thermoset Resins

Other characteristics

Brand: DISTITRON
End Uses: Pipes, Tanks
Polymer Name: Polyester (unspecified)
Color: Green
Markets: Automotive & Transportation
Industrial
Shelf LIfe: 6 Months (23°C in Dark )
Technology: Composite Materials
Composites End Use: Pipes
Tanks
Material Features: Improved Flexibility
HIGHLIGHTS: Medium flexibility and elasticity
Preaccelerated
Handling: Store in the shade, out of direct sunlight; Keep storage temperature below 25°C; Unseal container just before use; Shelf life will be reduced reaching higher temperature
Composite Materials Functions: Resins Binders & Matrix Materials

Technical data

Table 1 of 2

6 rows

Characteristic	Value	Unit	Method
Solid Content	61 - 65	%	MT-CU001C
Brookfield Viscosity at 25°C, sp 2 rpm 20	380 - 470	mPa.s	MT-CU025V
Specific weight at 20°C	1,11	g/cm3	—
Peak at 25°C + 2% PBO50	9:30 - 12:30	minutes	RS.03.G
Exothermic peak at 25°C + 2% PBO50	100 - 120	°C	RS.03.G
Acidity at 25°C + 2% PBO50	21 - 28	mg KOH/g	MT-CU001I

Table 2 of 2

3 rows

Characteristic	Value	Unit	Method
Tensile strength at 23°C for 4h /+ 16h at 70°C	18	MPa	ISO 527 (2012)
Tensile Modulus at 23°C for 4h /+ 16h at 70°C	1000	MPa	ISO 527 (2012)
Elongation at break at 23°C for 4h /+ 16h at 70°C	30,0	%	ISO 527 (2012)