POLYCOR® TOOLING PA CLEAR 0200
POLYCOR® TOOLING PA CLEAR 0200 - A pre-accelerated gel coat base on unsaturated polyester resin. It is cured using MEKP peroxide.This product is recommended for mold manufacturing process and provide durable surfaces to withstand the repeated moldings of GRP laminates.
Product families
Applications
Industrial — Chemical & Industrial Manufacturing
- Tooling & Moldmaking
Automotive & Transportation — Transportation
- Marine
Product Families
Composite Materials — Surface Finishes
- Gelcoats & Topcoats
Other characteristics
- Brand
- POLYCOR
- Color
- Black, Green, Orange
- Black
- Green
- Orange
- Features
Chemical Resistance, Chemical Resistant, Flame Retardant, High Impact Resistance
- Functions
- Surface Finish
- Markets
- Automotive & Transportation
- Industrial
- Technology
- Composite Materials
- Application Methods
- Spray
- Material Features
- Chemical Resistant
- Flame Retardant
- High Impact Resistance
- Shelf Life Storage
4 Months .. When the product is sealed in its original packing, stored indoors away from direct sunlight and direct heat sources and ideally at ambient temperature between 15°C and 25°C .
- Composite Materials Functions
- Surface Finish
Technical data
Table 1 of 3
3 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Elongation at break | 3,9 | % | ISO 527 |
| H.D.T (NFT ISO 75)......... | 79 | °C | — |
| Tensile strength | 45 | MPa | — |
Table 2 of 3
7 rows| Characteristic | Value | Unit |
|---|---|---|
| Density | 1,11 - 1,15 | — |
| Sag Resistance | 500 | μm - wet |
| Color | Depends colour | — |
| Hide depends colour | 700 - 900 | μm - wet |
| Viscosity (25°C - Spindle 5-5 rpm) | 100 - 150 | dPa.s |
| Thixotropic Index (5/50 rpm) | 6,0 - 7,5 | — |
| Solid Content (15mn at 150°C) | 51 - 55 | % |
Table 3 of 3
4 rows| Characteristic | Value | Unit |
|---|---|---|
| Peak Time (200g - 25°C - 1,8% MEKP) | 30 - 40 | mn |
| Film cure (500μ - 20°C - 2% MEKP) | 70 - 80 | mn |
| Gel Time (200g - 25°C - 1,8% MEKP) | 22 - 28 | mn |
| Peak exotherm (°C) (200g - 25°C - 1,8% MEKP) | 200 - 240 | — |