DISTITRON® 3519 A
DISTITRON® 3519 A - Unsaturated polyester resin in styrene,Orthophthalic. It is used to produce production of gelcoat through mix with fillers and/or additives.
Product families
Applications
Building & Construction — Building Envelope & Roofing
- Glazing & Window Elements
- Shingles & Tiles
Building & Construction — Building Materials
- Fence Decks & Rails
- Interior Fixtures
- Pipes & Plumbing
- Siding & Trim
- Structural Components
- Wall Panels
Industrial — Chemical & Industrial Manufacturing
- Equipment & Parts
Building & Construction — Infrastructure, Roads & Paving
- Pavement Highways Roads & Bridges
Industrial — Oil, Gas & Mining
- Refining & Gas Processing
Industrial — Power, Water & Utilities
- Power & Utilities
- Renewable Energy
Automotive & Transportation — Transportation
- Rail & Mass Transit
Product Families
Composite Materials — Polymers & Resins
- Thermoset Resins
Other characteristics
- Brand
- DISTITRON
- End Uses
- Pipes, Tanks
- Polymer Name
- Polyester (unspecified)
- Color
- Yellow
- Markets
- Automotive & Transportation
- Building & Construction
- Industrial
- Shelf LIfe
- 6 Months (23°C in Dark )
- Technology
- Composite Materials
- Composites End Use
- Pipes
- Tanks
- Material Features
- Good UV Protection
- HIGHLIGHTS
- Clear unaccelerated
- Light stabilized
- Handling
Store in the shade, out of direct sunlight; Keep storage temperature below 25°C; Unseal container just before use; Shelf life will be reduced reaching higher temperature
- Composite Materials Functions
- Resins Binders & Matrix Materials
Technical data
Table 1 of 2
6 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Solid Content | 65 - 69 | % | MT-CU001C |
| Brookfield Viscosity at 25°C, sp 2 rpm 20 | 580 - 720 | mPa.s | MT-CU025V |
| Gel Time at 25°C + 0,3% Co 6% + 0,8% MEKP50 | 21 - 26 | minutes | RS.08.G |
| Delta at 25°C + 0,3% Co 6% + 0,8% MEKP50 | 10-16 | minutes | RS.08.G |
| Exothermic peak at 25°C + 0,3% Co 6% + 0,8% MEKP50 | 150 - 180 | °C | RS.08.G |
| Specific weight at 20°C | 1,13 | g/cm3 | — |
Table 2 of 2
7 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Flexural strength at 23°C for 24h /+ 2h at 100°C /+ 1h at 100°C | 135 | MPa | ISO 178/B (2010) |
| Flexural modulus at 23°C for 24h /+ 2h at 100°C /+ 1h at 100°C | 4000 | MPa | ISO 178/B (2010) |
| Tensile strength at 23°C for 24h /+ 2h at 100°C /+ 1h at 100°C | 75 | MPa | ISO 527 (2012) |
| Barcol Hardness at 25°C at 23°C for 24h /+ 2h at 100°C /+ 1h at 100°C | 45 | — | ASTM D 2583 (2007) |
| Tensile Modulus at 23°C for 24h /+ 2h at 100°C /+ 1h at 100°C | 4000 | MPa | ISO 527 (2012) |
| HDT at 23°C for 24h /+ 2h at 100°C /+ 1h at 100°C | 64 | °C | ISO 75 -2A (2013) |
| Elongation at break at 23°C for 24h /+ 2h at 100°C /+ 1h at 100°C | 2,5 | % | ISO 527 (2012) |