NORSODYNE® O 12335 AL

Chemical Family: Polyesters, Unsaturated Polyester (UPE)PolyestersUnsaturated Polyester (UPE)

NORSODYNE® O 12335 AL - Unsaturated polyester resin in styrene,Orthophthalic. It is used to produce inclusion through casting method.

Product families

Building & Construction — Building Envelope & Roofing

Building & Construction — Building Materials

Industrial — Chemical & Industrial Manufacturing

Building & Construction — Infrastructure, Roads & Paving

Industrial — Oil, Gas & Mining

Industrial — Power, Water & Utilities

Composite Materials — Polymers & Resins

Brand: NORSODYNE
End Uses: Pipes, Structural Components, Tanks
Polymer Name: Polyester (unspecified)
Markets: Building & Construction
Industrial
Shelf LIfe: 6 Months (23°C in Dark )
Technology: Composite Materials
Composites End Use: Pipes
Structural Components
Tanks
Material Features: Good UV Protection
HIGHLIGHTS: Low reactivity
Low viscosity
Preaccelerated
Light stabilized
Handling: Store in the shade, out of direct sunlight; Keep storage temperature below 25°C; Unseal container just before use; Shelf life will be reduced reaching higher temperature
Composite Materials Functions: Resins Binders & Matrix Materials

5 rows

Characteristic	Value	Unit	Method
Brookfield Viscosity at 23°C, sp 2 rpm 50	310 - 390	mPa.s	MT-CU023V
Gel Time at 25°C + 1% Luperox K4CE	16 - 22	minutes	MT-CU019R
Peak at 25°C + 1% Luperox K4CE	45 -70	—	MT-CU019R
Exothermic peak at 25°C + 1% Luperox K4CE	150 - 175	°C	MT-CU019R
Solid Content	62,5 - 66,5	%	MT-CU001C

6 rows

Characteristic	Value	Unit	Method
Elongation at break at 40°C for 16h	1,4	%	ISO 527 (2012)
Flexural strength at 40°C for 16h	105	MPa	ISO 178 (2011)
Tensile strength at 40°C for 16h	40	MPa	ISO 527 (2012)
Tensile Modulus at 40°C for 16h	3500	MPa	ISO 527 (2012)
Flexural modulus at 40°C for 16h	3150	MPa	ISO 178 (2011)
HDT at 40°C for 16h/ +2h for 120°C	50	°C	ISO 75 -2A (2013)