NORSODYNE® H 84233 L
NORSODYNE® H 84233 L - Unsaturated polyester resin in styrene,halogenated. It is used to produce building panels,parts with high resistance to fire through hand lay up and spray up,continuous laminating method.
Product families
Applications
Building & Construction — Building Envelope & Roofing
- Glazing & Window Elements
- Shingles & Tiles
Building & Construction — Building Materials
- Fence Decks & Rails
- Interior Fixtures
- Pipes & Plumbing
- Siding & Trim
- Structural Components
- Wall Panels
Industrial — Chemical & Industrial Manufacturing
- Equipment & Parts
Building & Construction — Infrastructure, Roads & Paving
- Pavement Highways Roads & Bridges
Industrial — Oil, Gas & Mining
- Refining & Gas Processing
Industrial — Power, Water & Utilities
- Power & Utilities
- Renewable Energy
Automotive & Transportation — Transportation
- Rail & Mass Transit
Product Families
Composite Materials — Polymers & Resins
- Thermoset Resins
Other characteristics
- Brand
- NORSODYNE
- End Uses
- Pipes, Structural Components, Tanks
- Polymer Name
- Polyester (unspecified)
- Processing Methods
- Continuous Lamination, Hand Lay-up, Spray Lay-up
- Markets
- Automotive & Transportation
- Building & Construction
- Industrial
- Shelf LIfe
- 9 Months (23°C in Dark )
- Technology
- Composite Materials
- Product Safety
The final Fire resistance properties could change following the final structure of the piece and its use's condition. It will be necessary to verify the final properties on a prototype before industrial production.
- Application Methods
- Spray
- Composites End Use
- Pipes
- Structural Components
- Tanks
- Material Features
- Chemical Resistant
- Flame Retardant
- Good UV Protection
- HIGHLIGHTS
- Low viscosity
- Fire retardand properties
- Light stabilized
- Very good chemical resistance
- Handling
Store in the shade, out of direct sunlight; Keep storage temperature below 25°C; Unseal container just before use; Shelf life will be reduced reaching higher temperature
- Composite Materials Functions
- Resins Binders & Matrix Materials
- Composites Processing Methods
- Continuous Lamination
- Hand Lay-up
- Spray Lay-up
Technical data
Table 1 of 2
6 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Solid Content | 68 - 72 | % | MT-CU001C |
| Specific weight at 20°C | 1,10 | g/cm3 | — |
| Brookfield Viscosity at 23°C, sp 2 rpm 50 | 400 - 500 | mPa.s | MT-CU023V |
| Gel Time at 23°C + 1,2% Co 1% + 1,5% MEKP50 | 14 - 18 | minutes | MT-CU152R |
| Peak at 23°C + 1,2% Co 1% + 1,5% MEKP50 | 34 - 42 | — | MT-CU152R |
| Exothermic peak at 23°C + 1,2% Co 1% + 1,5% MEKP50 | 100 - 120 | °C | MT-CU152R |
Table 2 of 2
6 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Elongation at break at 40°C for 16h/ +2h for 90°C | 1,15 | % | ISO 527 (2012) |
| Flexural modulus at 40°C for 16h/ +2h for 90°C | 3500 | MPa | ISO 178 (2011) |
| Flexural strength at 40°C for 16h/ +2h for 90°C | 85 | MPa | ISO 178 (2011) |
| Tensile strength at 40°C for 16h/ +2h for 90°C | 40 | MPa | ISO 527 (2012) |
| Tensile Modulus at 40°C for 16h/ +2h for 90°C | 3600 | MPa | ISO 527 (2012) |
| HDT at 40°C for 16h/ +2h for 120°C | 82 | °C | ISO 75 -2A (2013) |