DISTITRON® 629 S
DISTITRON® 629 S - Unsaturated polyester resin in styrene,special. It is used to produce furnitures and sanitary through casting,to be used with trihydrate of alumina method.
Product families
Applications
Building & Construction — Building Envelope & Roofing
- Glazing & Window Elements
- Shingles & Tiles
Building & Construction — Building Materials
- Fence Decks & Rails
- Interior Fixtures
- Pipes & Plumbing
- Siding & Trim
- Structural Components
- Wall Panels
Building & Construction — Infrastructure, Roads & Paving
- Pavement Highways Roads & Bridges
Product Families
Composite Materials — Polymers & Resins
- Thermoset Resins
Other characteristics
- Brand
- DISTITRON
- Polymer Name
- Polyester (unspecified)
- Color
- Violet
- Markets
- Building & Construction
- Shelf LIfe
- 3 Months (23°C in Dark )
- Technology
- Composite Materials
- Product Safety
Store in the shade, out of direct sunlight. Keep storage temperature below 25°C. Unseal container just before use. Shelflife will be reduced reaching higher temperature.
- Material Features
- Good UV Protection
- HIGHLIGHTS
- Acrylic modified
- Preaccelerated
- Light stabilized
- Handling
Store in the shade, out of direct sunlight; Keep storage temperature below 25°C; Unseal container just before use; Shelf life will be reduced reaching higher temperature
- Composite Materials Functions
- Resins Binders & Matrix Materials
Technical data
Table 1 of 2
6 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Specific weight at 20°C | 1,12 | g/cm3 | — |
| Solid Content | 66 - 70 | % | MT-CU001C |
| Brookfield Viscosity at 25°C, sp 2 rpm 20 | 720 - 800 | mPa.s | MT-CU025V |
| Gel Time at 25°C + 2% MEKP50 | 6-10 | minutes | RS.08.G |
| Delta at 25°C + 2% MEKP50 | 5-9 | — | RS.08.G minutes |
| Exothermic peak at 25°C + 2% MEKP50 | 160 - 195 | °C | RS.08.G |
Table 2 of 2
7 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| HDT at 23°C for 24h /+ 2h at 100°C /+ 1h at 100°C | 70 | °C | ISO 75 -2A (2013) |
| Tensile Modulus at 23°C for 24h /+ 2h at 100°C /+ 1h at 100°C | 3300 | MPa | ISO 527 (2012) |
| Tensile strength at 23°C for 24h /+ 2h at 100°C /+ 1h at 100°C | 60 | MPa | ISO 527 (2012) |
| Flexural strength at 23°C for 24h /+ 2h at 100°C /+ 1h at 100°C | 110 | MPa | ISO 178/B (2010) |
| Flexural modulus at 23°C for 24h /+ 2h at 100°C /+ 1h at 100°C | 3900 | MPa | ISO 178/B (2010) |
| Barcol Hardness at 25°C at 23°C for 24h /+ 2h at 100°C /+ 1h at 100°C | 44 | — | ASTM D 2583 (2007) |
| Elongation at break at 23°C for 24h /+ 2h at 100°C /+ 1h at 100°C | 3,2 | % | ISO 527 (2012) |