NORSODYNE® C 55377 AL
NORSODYNE® C 55377 AL - Unsaturated polyester resin in styrene,Isophthalic-Neopentylic. It is used to produce agglomerated and engineered stones through casting method.
Product families
Applications
Building & Construction — Building Envelope & Roofing
- Glazing & Window Elements
- Shingles & Tiles
Building & Construction — Building Materials
- Fence Decks & Rails
- Interior Fixtures
- Pipes & Plumbing
- Siding & Trim
- Structural Components
- Wall Panels
Building & Construction — Infrastructure, Roads & Paving
- Pavement Highways Roads & Bridges
Product Families
Composite Materials — Polymers & Resins
- Thermoset Resins
Other characteristics
- Brand
- NORSODYNE
- End Uses
- Structural Components
- Polymer Name
- Polyester (unspecified)
- Markets
- Building & Construction
- Shelf LIfe
- 6 Months (23°C in Dark )
- Technology
- Composite Materials
- Composites End Use
- Structural Components
- Material Features
- Good UV Protection
- HIGHLIGHTS
- Light stabilized
- Handling
Store in the shade, out of direct sunlight; Keep storage temperature below 25°C; Unseal container just before use; Shelf life will be reduced reaching higher temperature
- Composite Materials Functions
- Resins Binders & Matrix Materials
Technical data
Table 1 of 2
5 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Solid Content | 70 - 74 | % | MT-CU001C |
| Gel Time at 23°C + 1,5% MEKP50 | 10-12 | minutes | MT-CU151R |
| Exothermic peak at 23°C + 1,5% MEKP50 | 125 - 145 | °C | MT-CU151R |
| Brookfield Viscosity at 23°C, sp 3 rpm 50 | 1000 - 1200 | mPa.s | MT-CU023V |
| Peak at 23°C + 1,5% MEKP50 | 25 - 31 | — | MT-CU151R minutes |
Table 2 of 2
6 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile strength at 40°C for 16h/ +2h for 90°C | 70 | MPa | ISO 527 (2012) |
| Tensile Modulus at 40°C for 16h/ +2h for 90°C | 3520 | MPa | ISO 527 (2012) |
| Elongation at break at 40°C for 16h/ +2h for 90°C | 4 | % | ISO 527 (2012) |
| Flexural strength at 40°C for 16h/ +2h for 90°C | 140 | MPa | ISO 178 (2011) |
| Flexural modulus at 40°C for 16h/ +2h for 90°C | 4150 | MPa | ISO 178 (2011) |
| HDT at 40°C for 16h/ +2h for 120°C | 67 | °C | ISO 75 -2A (2013) |