Denka Company ABS glass fiber reinforced K-5110G

Chemical Family: Acrylonitrile Butadiene Styrene (ABS)Styrenics

ABS glass fiber reinforced K-5110G has an excellent heat resistant property, which can be used as a substitute for engineering plastics as well as in various other fields. In general, this type of ABS resin has one disadvantage of having a poor surface finish; however, DENKA has developed a special technique to improve its surface texture by optimizing the fiber length distribution of a base resin and glass fibers.

Product families

Applications

Building & Construction — Building Materials

Structural Components

Industrial — Chemical & Industrial Manufacturing

Equipment & Parts

Product Families

Plastics — Basic Thermoplastics

Styrenics

Other characteristics

Polymer Name: Acrylonitrile Butadiene Styrene (ABS)
Fillers Included: Glass Fiber
Markets: Building & Construction
Industrial
Flame Rating: UL 94 HB
Technology: Plastics
Products Outline: A versatile ABS (acrylonitrile butadien styrene) resin.
Material Features: Heat Resistance
Non Smooth Surface Finish
Certifications and Compliance: UL 94
Plastics and Elastomers End Uses: Scr Structural Components
Plastics and Elastomers Functions: Resin

Technical data

Table 1 of 1

21 rows

Characteristic	Value	Unit	Method
Melt Mass Flow Rate (220°C 98N)	0.6	g/10min	ISO 1133
Melt Mass Flow Rate (265°C 98N)	14	g/10min	ISO 1133
Tensile Modulus (1mm/min)	4000	MPa	ISO 527-1, -2
Tensile Stress at Break (50mm/min)	58	MPa	ISO 527-1, -2
Flexural Modulus (2mm/min)	3800	MPa	ISO 178
Flexural Strength (2mm/min)	97	MPa	ISO 178
Charpy Impact Strength Notched	8	kJ/m2	ISO 179
Temperature of Deflection (under load 1.8MPa Flatwise)	129	°C	ISO 75-1, -2
Vicat Softening Temperature (50N)	135	°C	ISO 306
Vicat Softening Temperature (50N)	134	°C	ASTM D-1525
Rockwell Hardness R-scale	115	—	ISO 2039-2
Rockwell Hardness R-scale	120	—	ASTM D-785