Yuyao Zhongfa Engineering Plastics 66G30
- Chemical Family
- Polyamides
Yuyao Zhongfa Engineering Plastics 66G30 is a grade of Reinforced Flame Retardant Polycaprolactam which offers high mechanical properties, good heat resistance, good dimensional stability, good flammability, good processibility. Reinforced flame retardant PA66 is used for automotive parts, furniture parts, electric tool, transformer skeleton, thin-walled relay, electric device parts, residual current operated protective devices, electrical appliances parts, vision parts, etc.
Product families
Applications
Applications
- Consumer Goods — Appliances & Electronics; Consumer Goods — Furniture; Electrical & Electronics — Other Electrical & Electronics Applications
Automotive & Transportation — Automotive
- Exterior & Body
- Interior
Electrical & Electronics — Devices & Assemblies
- Consumer Electronics
Electrical & Electronics — Parts & Components
- Switches & Relays
Electrical & Electronics — Wire & Cable
- Power Transmission & Distribution
Product Families
Plastics — Engineering & Specialty Polymers
- Polyamides
Other characteristics
- Polymer Name
- Polyamide 66 (PA 66)
- Fillers Included
- Glass Fiber
- Flexural Modulus
- 6800.0 - 6800.0 MPa
- Additives Included
- Flame Retardant
- Markets
- Automotive & Transportation
- Consumer Goods
- Electrical & Electronics
- Technology
- Plastics
- Material Features
- Dimensional Stability
- Flame Retardant
- Good Flammability Properties
- Good Mechanical Properties
- Good Processability
- Heat Resistance
- Non-Halogenated
- Plastics and Elastomers End Uses
- Automotive Components
- Automotive Exterior Parts
- Automotive Interior Parts
- Furniture
- Relay Bases
- Tool/Tote Box
- Plastics and Elastomers Functions
- Resin
- Reinforced Flame Retardant Processing Conditions
Injection temperature 235~275℃, mold temperature 60-90 ℃,injection pressure 60-100MPa, eliminate moisture at 85-90 ℃ for 6-8 hours.
Technical data
Table 1 of 1
9 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Density | 1.35 | g/cm3 | D792 |
| Tensile Strength | 145.0 | MPa | D638 |
| Tensile Elongation | 3.0 | % | D638 |
| Flexural Strength | 240.0 | MPa | D790 |
| Flexural Modulus | 6800.0 | MPa | D790 |
| Notched Charpy Impact Strength | 14.0 | KJ/m2 | D256 |
| Heat Deflection Temperature (1.82MPa) | 240.0 | ℃ | D648 |
| Volume Resistivity | 1015.0 | Ω.cm | D257 |
| Molding Shrinkage | 0.3-0.6 | % | D955 |