Yuyao Zhongfa Engineering Plastics FR-88E
- Chemical Family
- High-Impact Polystyrene (HIPS)Styrenics
Yuyao Zhongfa Engineering Plastics FR-88E is a grade of Flame Retardant High Impact Polystyrene which offers good flammability, good aging resistance, good thermal stability, high mechanical properties, easy flow and good process ability. Flame Retardant HIPS is used for TV housing, electric appliance shells, electric plug-in unit, electric switch, housing for electrical appliances, communications equipment's, decorative lighting, etc.
Product families
Applications
Applications
- Consumer Goods — Appliances & Electronics
Electrical & Electronics — Devices & Assemblies
- Consumer Electronics
- Lighting
Electrical & Electronics — Parts & Components
- Housings & Enclosures
- Switches & Relays
Electrical & Electronics — Wire & Cable
- Data Communication Cables
Product Families
Plastics — Basic Thermoplastics
- Styrenics
Other characteristics
- Polymer Name
- High Impact Polystyrene (HIPS)
- Additives Included
- Flame Retardant
- Markets
- Consumer Goods
- Electrical & Electronics
- Technology
- Plastics
- Material Features
- Consistent Performance
- Flame Retardant
- Good Flammability Properties
- Good Flow
- Good Mechanical Properties
- Good Processability
- Good Thermal Stability
- Non-Halogenated
- Plastics and Elastomers End Uses
- Communication Applications
- Housings
- Lighting Applications
- Switch Base
- Plastics and Elastomers Functions
- Resin
- Flame Retardant HIPS Processing Conditions
Injection temperature 190-225℃, mold temperature 50-80℃, injection pressure 60-80MPa, eliminate moisture at 85-90℃ for 4-5 hours.
Technical data
Table 1 of 1
12 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Density | 1.18 | g/cm3 | D792 |
| Tensile Strength | 25.3 | MPa | D638 |
| Tensile Elongation | 23.0 | % | D638 |
| Flexural Strength | 42.0 | MPa | — |
| Flexural Modulus | 1800.0 | MPa | D790 |
| Notched Charpy Impact Strength | 9.5 | KJ/m2 | D256 |
| Rockwell Hardness | 89.0 | HRR | — |
| Heat Deflection Temperature (1.82MPa) | 83.0 | ℃ | D648 |
| Flame Resistance Properties | V-0 | 1.6mm | UL94 |
| Vicat Softening Point | 96.0 | ℃ | D1525 |
| Melt Index | 4.0 | g/10min | D1238 |
| Molding Shrinkage | 0.5-0.8 | % | D955 |