- Chemical Family
- Polyethylene Cross-Linked (PEX)Polyethylenes
3H Vinacom XLPE compound 3H VINACOM HA-5010 is a silane cross-linkable polyethylene compound for low voltage electrical wire and cable insulation. Both the grafting and wire coating process are performed in one single step in the usual wire and cable production extruder for polyethylene and cross-linking takes place through a reaction involving water vapor after being extruded. Difficulty in maintaining dimensional accuracy during cross-linking is avoided because the temperature of cross-linking is below the crystalline melting point of the polymer. Therefore, 3H VINACOM XLPE HA-5010 allow cross-linked polyethylene wire and cable without the need for much capital in special equipment like peroxide or radiation cross-linking.
Product families
Applications
Electrical & Electronics — Wire & Cable
- Building Wires & Power Cables
Product Families
Plastics — Thermoset Resins
- Other Thermoset Resins
Other characteristics
- End Uses
- Cables
- Polymer Name
- Crosslinked Polyethylene (XLPE / PEX)
- Tensile Strength
- 0.01911 - 0.01911 MPa
- Processing Methods
- Extrusion
- Markets
- Electrical & Electronics
- Technology
- Plastics
- Packaging Type
- Bags
- Material Features
- Dimensional Stability
Technical data
Table 1 of 2
8 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Density at 23% | 0.92 -0.94 | g/cm3 | ISO 1183 |
| Elongation at Break | 620 | % | IEC 60502 TCVN 5935 |
| HOT (200ºC 0.2 Mpa) | 95 | % | IEC 60502 TCVN 5935 |
| Retention of Elongation break (After aging (136°C x 168Hrs)) | 90 | % | IEC 60502 TCVN 5935 |
| Retention of Tensile strength (After aging (136°C x 168Hrs)) | 95 | % | IEC 60502 TCVN 5935 |
| SET(200ºC 0.2 Mpa) | 5 | % | IEC 60502 TCVN 5935 |
| Shrinkage | 0.0-2.5 | % | IEC 60502 TCVN 7447:1998 |
| Tensile strength | 1.95 | g/mm2 | IEC 60502 TCVN 5935 |
Table 2 of 2
3 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Dielectric Constant, 1KHz | 2.3 | — | ASTM D 150 |
| Dissipation Factor, 60 Hz | 0.00025 | — | ASTM D 150 |
| Volume Resistivity at 20°C | 1.0 x 10^15 | Ω.cm | IEC 60502 TCVN 5935 |