Xp³® 72-1111
Xp³® 72-1111 is a Multi-purpose calcium sulfonate grease.
Identification
Product families
Applications
- Equipment & Parts
Product Families
- Greases
Other characteristics
- Brand
- Xp³
- Features
Corrosion Resistant, Excellent Mechanical Strength, High Loading Absorption Capability, Oxidation Resistant, Water Resistant, Wide Temperature Operating Range
- Product Type
- Grease
- Thickener Type
- Calcium Sulfonate Complex
- Application Area
Bearings, Electric Motors, Machine Parts, Rotary Joints; Bearings; Electric Motors; Machine Parts; Rotary Joints
- Markets
- Industrial
- Technology
- Ready-to-Use Products
- Characteristic
A calcium sulfonate grease that was created using new formulation technology. Exceptional mechanical stability.; Functions well under very high loads (high E.P.); Rejects water; Resists oxidation and inhibits corrosion; Performs extremely well at temperatures within its performance range of -40ºC to 250ºC
- Typical Applications
Bearings exposed to water (such as wet end of paper machine); Calendar rolls; Heavy machinery; Fifth wheel; Roll bearings; Industrial equipment in an adverse environment or under heavy load; Bearing operating at low or high rpm; Electric motors; Rotary joints
- Ready to Use Product Features
- Corrosion Resistant
- Excellent Mechanical Strength
- High Loading Absorption Capability
- Oxidation Resistant
- Water Resistant
- Wide Temperature Operating Range
Technical data
Table 1 of 1
16 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| N.L.G.I. Grade | 2.0 | — | D217 |
| Penetration (25°C, 60 stokes) | 275.0 | — | — |
| Dropping Point | 300.0 | °C | — |
| Oil Separation (24 hours, 25°C) | 0.1 | % | — |
| Oxidation Resistance Loss of Pressure (100 hrs.) | 0.0 | PSI | D-942 |
| Oxidation Resistance Loss of Pressure (500 hrs.) | 2.0 | PSI | D-942 |
| Oxidation Resistance Loss of Pressure (1,000 hrs.) | 9.0 | PSI | D-942 |
| Roll Stability Penetration | 19.0 | — | D-1831 |
| 4 Ball Wear Test Scar (75°C, 40 kg, 1200 rpm, 1h) | 0.39 | mm | D-2266 |
| 4 ball EP Test - LWI | 500.0 | kg | D-2596 |
| Timken OK Load | 65.0 | lbs | D-2509 |
| Rust Test Rating | 1,1,1 | — | D-1743 |