Xp³® 72-1113
Xp³® 72-1113 is High performance synthetic slow melt high-temp grease for industrial equipment.
Identification
Product families
Applications
- Equipment & Parts
Product Families
- Greases
Other characteristics
- Brand
- Xp³
- Features
Corrosion Resistant, Excellent Mechanical Strength, High Loading Absorption Capability, High Temperature Resistance, Oxidation Resistant, Water Resistant
- Product Type
- Grease
- Thickener Type
- Calcium Sulfonate Complex
- Application Area
Bearings, Electric Motors, Machine Parts, Rotary Joints; Bearings; Electric Motors; Machine Parts; Rotary Joints
- Markets
- Industrial
- Additives
- EP, AW, AOX
- Technology
- Ready-to-Use Products
- Base Oil
- Synthetic Oil
- Characteristic
A synthetic hybrid calcium sulfonate / inorganic soap grease.; Demonstrates exceptional mechanical stability; Resistance to continuous both high and extreme low temperatures -30 to + 260°C; Fully formulated with the latest in EP additive technology; Functions very well under high loads; Unique thickening structure; Virtually eliminates water washout; Resists oxidation and inhibits corrosion
- Typical Applications
Bearings exposed to high temperatures; Bearings exposed to water (such as wet end of paper machine); Calendar rolls; Heavy machinery; Gear boxes requiring greases; Roller bearings; Industrial equipment in an adverse environment or under heavy load; Bearing operating at low or high rpm; Electric motors; Rotary joints; Crusher Bearings; Fifth Wheel
- Ready to Use Product Features
- Corrosion Resistant
- Excellent Mechanical Strength
- High Loading Absorption Capability
- High Temperature Resistance
- Oxidation Resistant
- Water Resistant
Technical data
Table 1 of 1
16 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| N.L.G.I. Grade | 2.0 | — | D217 |
| Penetration (25°C, 60 stokes) | 275.0 | — | — |
| Dropping Point | 300.0 | °C | — |
| Oil Separation (24 hours, 25°C) | 0.1 | % | — |
| Oxidation Stability (100 hrs.) | 0.0 | PSI | D-942 |
| Oxidation Stability (500 hrs.) | 2.0 | PSI | D-942 |
| Oxidation Stability (1,000 hrs.) | 9.0 | PSI | D-942 |
| Roll Stability Penetration | 19.0 | — | D-1831 |
| 4 Ball Wear Test Scar (75°C, 40 kg, 1200 rpm, 1h) | 0.39 | mm | D-2266 |
| 4 ball EP Test - LWI | 500.0 | kg | — |
| Timken OK Load | 65.0 | lbs | — |
| Rust Test Rating | 1,1,1 | — | D-1743 |