ROTEC® ABS SE 5/02
- Chemical Family
- Acrylonitrile Butadiene Styrene (ABS)Styrenics
ROTEC® ABS SE 5/02 is ABS, injection molding grade, impact modified.
Properties
- Physical Form
- Granules
- Solid
Product families
Applications
Applications
- Automotive & Transportation — Other Automotive & Transportation Applications; Consumer Goods — Other Consumer Goods Applications; Electrical & Electronics — Other Electrical & Electronics Applications; Healthcare & Pharma — Other Healthcare & Pharma Applications
Agriculture & Feed — Agricultural Films
- Pipes & Hoses
Automotive & Transportation — Automotive
- Electrical & Electronic Systems
- Exterior & Body
- Other Automotive Applications
Building & Construction — Building Envelope & Roofing
- Other Building Envelope & Roofing Applications
Building & Construction — Building Materials
- Other Building Materials
Electrical & Electronics — Parts & Components
- Housings & Enclosures
Automotive & Transportation — Transportation
- Aerospace & Aviation
Product Families
Plastics — Basic Thermoplastics
- Styrenics
Other characteristics
- Brand
- ROTEC
- Polymer Name
- Acrylonitrile Butadiene Styrene (ABS)
- Additives Included
- Impact Modifier
- Processing Methods
- Extrusion, Injection Molding
- Markets
- Agriculture & Feed
- Automotive & Transportation
- Building & Construction
- Consumer Goods
- Electrical & Electronics
- Healthcare & Pharma
- Technology
- Plastics
- Material Features
- Flame Retardant
- Impact Modified
- Certifications and Compliance
- Halal
- Kosher
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Extrusion
- Injection Molding
Technical data
Table 1 of 3
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Water Absorption (23 °C, 50 % RH, 24 h) | 0.3 | % | DIN EN ISO 62 |
| Density (23 °C, 50 % RH) | 1.03 | g/cm³ | DIN EN ISO 1133 |
Table 2 of 3
8 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Elongation at Break (50 mm/min 23 °C) | 17 | % | DIN EN ISO 527 |
| Flexural Modulus (2 mm/min 23 °C) | 2300 | MPa | DIN EN ISO 178 |
| Flexural Strength (2 mm/min 23 °C) | 67 | MPa | DIN EN ISO 178 |
| Impact Strength (Charpy) | n.b. | kJ/m² | DIN EN ISO 179/1eU |
| Notched Impact Strength (Charpy at 80 x 10 x 4 23 °C) | 22 | kJ/m² | DIN EN ISO 179/1eA |
| Notched Impact Strength (Charpy at 80 x 10 x 4 23 °C) | 40 | kJ/m² | DIN EN ISO 179/1eA |
| Tensile Modulus (1 mm/min 23 °C) | 2100 | MPa | DIN EN ISO 527 |
| Tensile Strength (50 mm/min 23 °C) | 41 | MPa | DIN EN ISO 527 |
Table 3 of 3
7 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Flammability (own test) | HB | — | UL94 |
| Heat deflection temperature (HDT/B) | 86 | °C | DIN EN ISO 75-1 |
| Melt Mass-Flow Rate (MFR) | 6 | g/10 min | DIN EN ISO 1133 |
| Processing Shrinkage (220 °C, 10 kg) | 0.6 0.8 | % | DIN EN ISO 294-4 |
| Thermal Coefficient of Linear Expansion | 0.95 | 104 ∙ K-1 | ISO 11359-2 |
| Thermal conductivity | 0.17 | W/(K∙m) | ISO 11359-2 |
| Vicat Softening Temperature (B 50) | 93 | °C | DIN EN ISO 306 |