ROTEC® ABS SE 3
- Chemical Family
- Acrylonitrile Butadiene Styrene (ABS)Styrenics
ROTEC® ABS SE 3 is ABS, extrusion grade, impact modified.
Properties
- Physical Form
- Granules
- Solid
Product families
Applications
Applications
- Automotive & Transportation — Other Automotive & Transportation Applications; Consumer Goods — Other Consumer Goods Applications; Electrical & Electronics — Other Electrical & Electronics Applications; Healthcare & Pharma — Other Healthcare & Pharma Applications
Agriculture & Feed — Agricultural Films
- Pipes & Hoses
Automotive & Transportation — Automotive
- Electrical & Electronic Systems
- Exterior & Body
- Other Automotive Applications
Building & Construction — Building Envelope & Roofing
- Other Building Envelope & Roofing Applications
Building & Construction — Building Materials
- Other Building Materials
Electrical & Electronics — Parts & Components
- Housings & Enclosures
Product Families
Plastics — Basic Thermoplastics
- Styrenics
Other characteristics
- Brand
- ROTEC
- Polymer Name
- Acrylonitrile Butadiene Styrene (ABS)
- Processing Methods
- Extrusion
- Markets
- Agriculture & Feed
- Automotive & Transportation
- Building & Construction
- Consumer Goods
- Electrical & Electronics
- Healthcare & Pharma
- Technology
- Plastics
- Certifications and Compliance
- Halal
- Kosher
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Extrusion
Technical data
Table 1 of 3
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Water Absorption (23 °C, 50 % RH, 24 h) | 0.3 | % | DIN EN ISO 62 |
| Density (23 °C, 50 % RH) | 1.04 | g/cm³ | DIN EN ISO 1133 |
Table 2 of 3
9 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Elongation at Break (50 mm/min 23 °C) | 15 | % | DIN EN ISO 527 |
| Flexural Modulus (2 mm/min 23 °C) | 2450 | MPa | DIN EN ISO 178 |
| Flexural Strength (2 mm/min 23 °C) | 72 | MPa | DIN EN ISO 178 |
| Impact Strength (Charpy) | n.b. | kJ/m² | DIN EN ISO 179/1eU |
| Impact Strength (Charpy) | 90 | kJ/m² | DIN EN ISO 179/1eU |
| Notched Impact Strength (Charpy at 80 x 10 x 4 23 °C) | 6 | kJ/m² | DIN EN ISO 179/1eA |
| Notched Impact Strength (Charpy at 80 x 10 x 4 23 °C) | 16 | kJ/m² | DIN EN ISO 179/1eA |
| Tensile Modulus (1 mm/min 23 °C) | 2400 | MPa | DIN EN ISO 527 |
| Tensile Strength (50 mm/min 23 °C) | 46 | MPa | DIN EN ISO 527 |
Table 3 of 3
6 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Flammability own test) | HB | — | UL94 |
| Melt Mass-Flow Rate (MFR) | 15 | g/10 min | DIN EN ISO 1133 |
| Processing Shrinkage (220 °C, 10 kg) | 0.5 | % | DIN EN ISO 294-4 |
| Thermal Coefficient of Linear Expansion | 0.9 | 104 ∙ K-1 | ISO 11359-2 |
| Thermal conductivity | 0.18 | W/(K∙m) | ISO 11359-2 |
| Vicat Softening Temperature (B 50) | 101 | °C | DIN EN ISO 306 |