ROMILOY® 2720
- Chemical Family
- Polycarbonate (PC)PolyestersPolyethylene Terephthalate (PET)
ROMILOY® 2720 is PC/PET, injection molding grade, easy-flowing, impact-resistant, high heat resistance.
Properties
- Physical Form
- Granules
- Solid
Product families
Applications
Applications
- Automotive & Transportation — Other Automotive & Transportation Applications; Consumer Goods — Other Consumer Goods Applications; Electrical & Electronics — Other Electrical & Electronics Applications; Healthcare & Pharma — Other Healthcare & Pharma Applications
Automotive & Transportation — Automotive
- Electrical & Electronic Systems
- Other Automotive Applications
Building & Construction — Building Envelope & Roofing
- Other Building Envelope & Roofing Applications
Building & Construction — Building Materials
- Other Building Materials
Automotive & Transportation — Transportation
- Aerospace & Aviation
Product Families
Plastics — Engineering & Specialty Polymers
- Blends & Alloys
Other characteristics
- Brand
- ROMILOY
- Density
- 1220.0 - 1220.0 kg/m³
- Polymer Name
- PC/PET Alloy
- Flexural Modulus
- 2200.0 - 2200.0 MPa
- Processing Methods
- Injection Molding
- Markets
- Automotive & Transportation
- Building & Construction
- Consumer Goods
- Electrical & Electronics
- Healthcare & Pharma
- Technology
- Plastics
- Material Features
- Very Good Heat Resistance
- Certifications and Compliance
- Halal
- Kosher
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 3
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Density (23 °C, 50 % RH) | 1.22 | g/cm³ | DIN EN ISO 1133 |
Table 2 of 3
9 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Elongation at Break (50 mm/min 23 °C) | min. 50 | % | DIN EN ISO 527 |
| Flexural Modulus (2 mm/min 23 °C) | 2200 | MPa | DIN EN ISO 178 |
| Flexural Strength (2 mm/min 23 °C) | 80 | MPa | DIN EN ISO 178 |
| Flexural Strength at (3.5% Strain of the outer Fiber) | 70 | MPa | DIN EN ISO 178 |
| Impact Strength (Charpy) | n.b. | kJ/m² | DIN EN ISO 179/1eU |
| Notched Impact Strength (Charpy at 80 x 10 x 4 23 °C) | 13 | kJ/m² | DIN EN ISO 179/1eA |
| Notched Impact Strength (Charpy at 80 x 10 x 4 23 °C) | 52 | kJ/m² | DIN EN ISO 179/1eA |
| Tensile Modulus (1 mm/min 23 °C) | 2300 | MPa | DIN EN ISO 527 |
| Tensile Strength (50 mm/min 23 °C) | 57 | MPa | DIN EN ISO 527 |
Table 3 of 3
6 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Vicat Softening Temperature (B 50) | 125 | °C | DIN EN ISO 306 |
| Flammability own test) | HB | — | UL94 |
| Glow Wire Flammability Index (GWFI) | 800 | °C | DIN EN 60695-2-12 |
| Heat deflection temperature (HDT/A) | 94 | °C | DIN EN ISO 75-1 |
| Melt Mass-Flow Rate (MFR) | 30 | g/10 min | DIN EN ISO 1133 |
| Processing Shrinkage (220 °C, 10 kg) | 0.4 0.6 | % | DIN EN ISO 294-4 |