To catalogue
LURANYL® HT 190
- Chemical Family
- Polyamides
LURANYL® HT 190 is a PPE/PA, injection molding grade, high heat resistance, black.
Properties
- Physical Form
- Granules
- Solid
Product families
Applications
Applications
- Automotive & Transportation — Other Automotive & Transportation Applications; Consumer Goods — Other Consumer Goods Applications; Electrical & Electronics — Other Electrical & Electronics Applications; Healthcare & Pharma — Other Healthcare & Pharma Applications
Automotive & Transportation — Automotive
- Electrical & Electronic Systems
- Other Automotive Applications
Building & Construction — Building Envelope & Roofing
- Other Building Envelope & Roofing Applications
- Shingles & Tiles
Building & Construction — Building Materials
- Other Building Materials
Product Families
Plastics — Engineering & Specialty Polymers
- Blends & Alloys
Other characteristics
- Brand
- LURANYL
- Density
- 1050.0 - 1050.0 kg/m³
- Polymer Name
- PPO/Nylon Alloy
- Processing Methods
- Injection Molding
- Markets
- Automotive & Transportation
- Building & Construction
- Consumer Goods
- Electrical & Electronics
- Healthcare & Pharma
- Technology
- Plastics
- Material Features
- Very Good Heat Resistance
- Certifications and Compliance
- Halal
- Kosher
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 3
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Water Absorption (23 °C, 50 % RH, 24 h) | 0.4 | % | DIN EN ISO 62 |
| Density (23 °C, 50 % RH) | 1.05 | g/cm³ | DIN EN ISO 1133 |
Table 2 of 3
7 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Elongation at Break (50 mm/min 23 °C) | 90 | % | DIN EN ISO 527 |
| Flexural Strength (2 mm/min 23 °C) | 81 | MPa | DIN EN ISO 178 |
| Impact Strength (Charpy) | n.b. | kJ/m² | DIN EN ISO 179/1eU |
| Notched Impact Strength (Charpy at 80 x 10 x 4 23 °C) | 12 | kJ/m² | DIN EN ISO 179/1eA |
| Notched Impact Strength (Charpy at 80 x 10 x 4 23 °C) | 45 | kJ/m² | DIN EN ISO 179/1eA |
| Tensile Modulus (1 mm/min 23 °C) | 2050 | MPa | DIN EN ISO 527 |
| Tensile Strength (50 mm/min 23 °C) | 50 | MPa | DIN EN ISO 527 |
Table 3 of 3
6 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Flammability (own test) | HB | — | UL94 |
| Heat deflection temperature (HDT/A) | 120 | °C | DIN EN ISO 75-1 |
| Melt Volume-Flow Rate (MVR) | 20 | cm³/10 min | DIN EN ISO 1133 |
| Processing Shrinkage (220 °C, 10 kg) | 0.9 1.1 | % | DIN EN ISO 294-4 |
| Thermal Coefficient of Linear Expansion | 0.95 | 104 ∙ K-1 | ISO 11359-2 |
| Vicat Softening Temperature (B 50) | 180 | °C | DIN EN ISO 306 |