To catalogue
ROTEC® ASA T 115/04
- Chemical Family
- Styrenics
ROTEC® ASA T 115/04 is ASA, extrusion and injection molding grade, high-impact, good weather resistance, high heat resistance.
Product families
Applications
Applications
- Automotive & Transportation — Other Automotive & Transportation Applications; Consumer Goods — Other Consumer Goods Applications; Electrical & Electronics — Other Electrical & Electronics Applications; Healthcare & Pharma — Other Healthcare & Pharma Applications
Automotive & Transportation — Automotive
- Electrical & Electronic Systems
- Exterior & Body
- Interior
- Other Automotive Applications
Building & Construction — Building Envelope & Roofing
- Other Building Envelope & Roofing Applications
Building & Construction — Building Materials
- Other Building Materials
Product Families
Plastics — Basic Thermoplastics
- Styrenics
Other characteristics
- Brand
- ROTEC
- Polymer Name
- Acrylonitrile Styrene Acrylate (ASA)
- Processing Methods
- Extrusion, Injection Molding
- Markets
- Automotive & Transportation
- Building & Construction
- Consumer Goods
- Electrical & Electronics
- Healthcare & Pharma
- Technology
- Plastics
- Material Features
- Good Weather Stability
- Low Emissions
- Very Good Heat Resistance
- Certifications and Compliance
- Kosher
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Extrusion
- Injection Molding
Technical data
Table 1 of 3
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Water Absorption (23 °C, 50 % RH, 24 h) | 2500 | MPa | DIN EN ISO 178 |
| Density (23 °C, 50 % RH) | 7 | g/cm³ | DIN EN ISO 1133 |
Table 2 of 3
8 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Elongation at Break (50 mm/min 23 °C) | 30 | % | DIN EN ISO 527 |
| Flexural Modulus (2 mm/min 23 °C) | 1.06 | % | DIN EN ISO 1183 |
| Flexural Strength (2 mm/min 23 °C) | 0.3 | % | DIN EN ISO 62 |
| Impact Strength (Charpy) | 107 | — | DIN EN ISO 306 |
| Notched Impact Strength (Charpy at 80 x 10 x 4 23 °C) | 97 | °C | DIN EN ISO 75-1 |
| Tensile Modulus (1 mm/min 23 °C) | 2700 | MPa | DIN EN ISO 527 |
| Tensile Modulus (1 mm/min 23 °C) | 1800 | MPa | DIN EN ISO 527 |
| Tensile Strength (50 mm/min 23 °C) | 50 | MPa | DIN EN ISO 527 |
Table 3 of 3
7 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Burning Rate (23 °C - 55 °C) | max. 100 | mm/min | DIN 75200 |
| Flammability (own test) | HB | — | UL94 |
| Heat deflection temperature (HDT/A) | 80 | MPa | DIN EN ISO 178 |
| Processing Shrinkage (220 °C, 10 kg) | 0.4 0.6 | % | DIN EN ISO 294-4 |
| Thermal Coefficient of Linear Expansion | 0.85 | 104 ∙ K-1 | ISO 11359-2 |
| Thermal conductivity | 0.17 | W/(K∙m) | ISO 11359-2 |
| Vicat Softening Temperature (B 50) | 12 | kJ/m² | DIN EN ISO 179/1eA |