ROMILOY® 9170E
ROMILOY® 9170E is PC/ABS, extrusion and injection molding grade, chlorine-, bromine- and antimon-free flame retardant.
Properties
- Physical Form
- Granules
- Solid
Product families
Applications
Applications
- Automotive & Transportation — Other Automotive & Transportation Applications; Consumer Goods — Other Consumer Goods Applications; Electrical & Electronics — Other Electrical & Electronics Applications; Healthcare & Pharma — Other Healthcare & Pharma Applications
Automotive & Transportation — Automotive
- Electrical & Electronic Systems
- Other Automotive Applications
Building & Construction — Building Envelope & Roofing
- Other Building Envelope & Roofing Applications
Building & Construction — Building Materials
- Other Building Materials
Product Families
Plastics — Engineering & Specialty Polymers
- Blends & Alloys
Other characteristics
- Brand
- ROMILOY
- Density
- 1180.0 - 1180.0 kg/m³
- Polymer Name
- PC/ABS Alloy
- Flexural Modulus
- 2550.0 - 2550.0 MPa
- Processing Methods
- Injection Molding
- Markets
- Automotive & Transportation
- Building & Construction
- Consumer Goods
- Electrical & Electronics
- Healthcare & Pharma
- Technology
- Plastics
- Additives Included
- Flame Retardant
- Material Features
- Flame Retardant
- Certifications and Compliance
- Halal
- Kosher
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 4
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Water Absorption (23 °C, 50 % RH, 24 h) | 0.3 | % | DIN EN ISO 62 |
| Density (23 °C, 50 % RH) | 1.18 | g/cm³ | DIN EN ISO 1133 |
Table 2 of 4
7 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Elongation at Break (50 mm/min 23 °C) | 30 | % | DIN EN ISO 527 |
| Flexural Modulus (2 mm/min 23 °C) | 2550 | MPa | DIN EN ISO 178 |
| Flexural Strength (2 mm/min 23 °C) | 92 | MPa | DIN EN ISO 178 |
| Impact Strength (Charpy) | n.b. | kJ/m² | DIN EN ISO 179/1eU |
| Notched Impact Strength (Charpy at 80 x 10 x 4 23 °C) | 29 | kJ/m² | DIN EN ISO 179/1eA |
| Tensile Modulus (1 mm/min 23 °C) | 2570 | MPa | DIN EN ISO 527 |
| Tensile Strength (50 mm/min 23 °C) | 58 | MPa | DIN EN ISO 527 |
Table 3 of 4
8 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Flammability (own test) | V0,5VB | — | UL94 |
| Glow Wire Flammability Index (GWFI) | 960 | °C | DIN EN 60695-2-12 |
| Glow Wire Ignition Temperature (GWIT) | 700 | °C | DIN EN 60695-2-13 |
| Heat deflection temperature (HDT/A) | 85 | °C | DIN EN ISO 75-1 |
| Melt Mass-Flow Rate (MFR) | 12 | g/10 min | DIN EN ISO 1133 |
| Processing Shrinkage (220 °C, 10 kg) | 0.4 | % | DIN EN ISO 294-4 |
| Thermal Coefficient of Linear Expansion | 0.8 | 104 ∙ K-1 | ISO 11359-2 |
| Vicat Softening Temperature (B 50) | 104 | °C | DIN EN ISO 306 |
Table 4 of 4
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Comparative Tracking Index (CTI) | 600 | V | DIN EN 60112 |