LURANYL® KR 2452-3
- Chemical Family
- Styrenics
LURANYL® KR 2452-3 is a PPE/PS-I, extrusion and injection molding grade, high heat resistance, nonhalogen flame retardant.
Properties
- Physical Form
- Solid
Product families
Applications
Applications
- Automotive & Transportation — Other Automotive & Transportation Applications; Consumer Goods — Other Consumer Goods Applications; Electrical & Electronics — Other Electrical & Electronics Applications; Healthcare & Pharma — Other Healthcare & Pharma Applications
Automotive & Transportation — Automotive
- Electrical & Electronic Systems
- Other Automotive Applications
Building & Construction — Building Envelope & Roofing
- Other Building Envelope & Roofing Applications
- Shingles & Tiles
Building & Construction — Building Materials
- Other Building Materials
Product Families
Plastics — Engineering & Specialty Polymers
- Blends & Alloys
Other characteristics
- Brand
- LURANYL
- Polymer Name
- PPO/PS Alloy
- Processing Methods
- Injection Molding
- Markets
- Automotive & Transportation
- Building & Construction
- Consumer Goods
- Electrical & Electronics
- Healthcare & Pharma
- Technology
- Plastics
- Labeling Claims
- Halogen-free
- Additives Included
- Flame Retardant
- Material Features
- Flame Retardant
- Very Good Heat Resistance
- Certifications and Compliance
- Halal
- Kosher
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 3
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Water Absorption (23 °C, 50 % RH, 24 h) | 11 | kJ/m² | DIN EN ISO 179/1eA |
| Density (23 °C, 50 % RH) | 15 | kJ/m² | DIN EN ISO 179/1eA |
Table 2 of 3
9 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Flexural Modulus (2 mm/min 23 °C) | 1.07 | g/cm³ | DIN EN ISO 1183 |
| Flexural Strength (2 mm/min 23 °C) | max. 0.15 | % | DIN EN ISO 62 |
| Impact Strength (Charpy) | MPa | — | DIN EN ISO 178 |
| Impact Strength (Charpy) | 115 | MPa | DIN EN ISO 178 |
| Notched Impact Strength (Charpy at 80 x 10 x 4 23 °C) | 118 | °C | DIN EN ISO 75-1 |
| Notched Impact Strength (Charpy at 80 x 10 x 4 23 °C) | 138 | °C | DIN EN ISO 306 |
| Tensile Modulus (1 mm/min 23 °C) | 2600 | MPa | DIN EN ISO 527 |
| Tensile Strain at Break | 6 | % | DIN EN ISO 527 |
| Tensile Strength (50 mm/min 23 °C) | 65 | MPa | DIN EN ISO 527 |
Table 3 of 3
5 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Flammability (own test) | V1 | — | UL94 |
| Melt Volume-Flow Rate (MVR) | 26 | cm³/10 min | DIN EN ISO 1133 |
| Processing Shrinkage (220 °C, 10 kg) | 0.5 - 0.7 | % | DIN EN ISO 294-4 |
| Thermal Coefficient of Linear Expansion | 10 ∙ K | 104 ∙ K-1 | ISO 11359-2 |
| Thermal conductivity | 0.18 | W/(K∙m) | ISO 11359-2 |