Vinavil 2841
- CASE Ingredients Features
- Good Peeling StrengthGood TackHigh Solid ContentTransparencyUV Resistance
- Chemical Family
- Acrylics & Acrylates
Vinavil 2841 is a high solids pure acrylic polymer emulsion with high peel adhesion. It coats well on silicone-coated release paper.
Properties
- Physical Form
- Emulsion
- Liquid
Identification
- CASE Ingredients Functions
- Binder & Resin
Product families
Applications
- Tape & Label Adhesives
- Tapes & Labels
Product Families
- Acrylics
Other characteristics
- Brand
- Vinavil
- End Uses
- Pressure Sensitive Adhesive, Waterborne Adhesive
- Features
Good Peeling Strength, Good Tack, High Solid Content, Transparency, UV Resistance
- Compatible Substrates & Surfaces
Double Sided Tapes, Film, Foam, Silicone Coated Papers, Textiles
- Markets
- Adhesives & Sealants
- Printing & Packaging
- Shelf LIfe
- 1 year
- Technology
- CASE Ingredients
- Packaging Type
- Bulk
- Drums
- Totes (IBC)
- Product Features
Vinavil 2841 can be thickened without thickeners up to 150,000 cps enabling it to be run on a conventional knife/bar over a roll coated head.
- Storage Condition
Vinavil 2841 must be stored at a temperature range between +5°C and +40°C in appropriate containers.
- Emulsifying System
- Anionic
- Product Performance
(1 mil polyester film, 1 mil dry thickness adhesive). 180° peel adhesion to stainless steel (oz/in): 55 Tack, rolling ball (cm): 3 Delaminating cardboard 1810A: 75%
- Chemical Inventories
- DSL (Canada)
- TSCA (USA)
- Applications
Vinavil 2841can be profitably used as pressure sensitive water based adhesives for films, double sided tapes, foams, textiles and labels.
- Packaging Information
Vinavil 2841 is available in bulk (20,000 L), totes (1000 L) and in drums (200 kg).
- Compatible Substrates and Surfaces
- Double Sided Tapes
- Film
- Foam
- Silicone Coated Papers
- Textiles
- Adhesives And Sealants
- Pressure Sensitive Adhesive
- Waterborne Adhesive
Technical data
Table 1 of 3
6 rows| Characteristic | Value | Unit |
|---|---|---|
| Density (at 20°C) | 1.04 | g/cm³ |
| Minimum Film - Forming Temperature (MFFT) | 0.0 | °C |
| Prevailing Particle Size | 0.28 | μm |
| Glass Transition Temperature | -41.0 | °C |
| Unreacted Monomers | max. 0.07 | % |
| Freeze/Thaw Stability | 5 cycles | — |
Table 2 of 3
1 row| Characteristic | Value |
|---|---|
| Aspect | Transparent, high tack, good u/v resistance. |
Table 3 of 3
3 rows| Characteristic | Value | Unit |
|---|---|---|
| Solid Content | 61.0 | % |
| Brookfield Viscosity (at 20°C, RVT model, Spindle 4/20 rpm) | 1500 | cPs |
| pH Value | 5.5 | — |