To catalogue
Cardolite® Lite 2001
- CASE Ingredients Features
- High Viscosity
- Chemical Family
- Phenalkamines
Cardolite® Lite 2001 is a light-colored, high viscosity 100% solids curing agent with excellent anticorrosion.
Identification
- CASE Ingredients Functions
- Curing Agent
Product families
Applications
Paints & Coatings — Automotive & Transportation
- Marine Coatings
Paints & Coatings — Building & Construction
- Concrete Coatings & Stains
- Floor Coatings
Automotive & Transportation — Coatings & Finishes
- Marine Coatings
Building & Construction — Flooring & Surfaces
- Floor Coatings
Paints & Coatings — Industrial Coatings
- Industrial Coatings
- Metal Coatings
Paints & Coatings — Packaging Coatings
- Primers & Lacquers
Automotive & Transportation — Transportation
- Marine
Product Families
CASE Ingredients — Additives
- Functional Additives
Other characteristics
- Brand
- Cardolite
- End Uses
Anti-Corrosion Coating, Primer, Solventless & High Solids Coating
- Features
- High Viscosity
- Functions
- Curing Agent
- Labeling Claims
- Solvent-free
- Markets
- Automotive & Transportation
- Building & Construction
- Paints & Coatings
- Appearance
- Light yellow
- Technology
- CASE Ingredients
- Coating End Applications
- Anti-Corrosion Coating
- Primer
- Solventless & High Solids Coating
- Compatible Substrates and Surfaces
- Concrete
Technical data
Table 1 of 1
10 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Viscosity (at 25°C) | 25000 - 50000 | cPs | ASTM D2196 |
| Technology | Phenalkamine | — | — |
| Color | max. 10 | Gardner | ASTM D1544 |
| Amine Value | 330.0 | mg KOH/g | ASTM D2074 |
| Gel Time (at 25°C, 50 g) | 75.0 | minutes | — |
| Thin Film Dry Hard Time (at 25°C, at 200 micron) | 3.0 | hours | ASTM D5895 |
| Thin Film Dry Hard Time (at 5°C, at 200 micron) | 12.5 | hours | ASTM D5895 |
| Thin Film Dry Hard Time (at 0°C, at 200 micron) | 19.0 | hours | ASTM D5895 |
| Theoretical Active Hydrogen Equivalent (based on total product weight) | 132.0 | — | — |
| Solid Content | 100.0 | % | — |