Hauthane HD-2602
- CASE Ingredients Features
- Abrasion ResistanceAir DryingExcellent AdhesionHigh PerformanceLow Surface TensionSlip Resistance
- Chemical Family
- Polyesters, Polyurethanes (PU)PolyestersPolyurethanes (PU)
Hauthane HD-2602 is an aliphatic, silicone-modified, polyester-based, water-borne polyurethane dispersion.
Properties
- Physical Form
- Dispersion
Identification
- CASE Ingredients Functions
- Binder & Resin
Product families
- Polyurethanes (PU)
Other characteristics
- Brand
- Hauthane
- End Uses
- Top Coat
- Features
Abrasion Resistance, Air Drying, Excellent Adhesion, High Performance, Low Surface Tension, Slip Resistance
- Compatible Substrates & Surfaces
- Metal, Plastics, Textiles
- Drying
Hauthane HD-2602 can be air dried, if desired, depending on film thickness. Typical oven drying temperatures and dwell times for aqueous coatings are sufficient to produce optimal film properties.
- Carrier
- N-Methyl Pyrrolidone
- Water
- Cure
- Air Dry
- Technology
- CASE Ingredients
- Suggested Use
Hauthane HD-2602 was designed primarily for topcoat applications where slip and abrasion resistance properties are required. Hauthane HD-2602 contains a non-fugitive silicone component that provides low surface tension characteristics on flexible and rigid substrates including plastics, metals and textiles.
- Application Methods
- Gravure Coating
- Spray
- Chemical Inventories
- DSL (Canada)
- TSCA (USA)
- Applications
Hauthane HD-2602 may be used as a sole vehicle or blended with acrylic emulsions for spray or rotogravure applications. Rheology modifications can be made with associative thickeners for alternative application methods.
- Product Characteristic
May be formulated into low surface tension coatings; Excellent abrasion resistance; Non-fugitive silicone component; Crosslinkable for improved adhesion and performance; Contains n-methyl pyrrolidone co-solvent
- Coating End Applications
- Top Coat
- Compatible Polymers and Resins
- Acrylics
- Compatible Substrates and Surfaces
- Metal
- Plastics
- Textiles
Technical data
Table 1 of 2
8 rows| Characteristic | Value | Unit |
|---|---|---|
| Solid Content | 34 - 36 | % |
| Viscosity | 50 - 500 | cPs |
| pH | 7.0 - 9.5 | — |
| Density | 8.7 | Ibs/gal |
| Softening Point | 305 | °F |
| Volatile Organic Compounds (as Supplied) | 105 | gm/l |
| Volatile Organic Compounds (less Water) | 243 | gm/l |
| Sward Hardness | 35 | — |
Table 2 of 2
5 rows| Characteristic | Value | Unit |
|---|---|---|
| 100% Modulus (Tested at 20 Inches/minute) | 3180 | psi |
| 200% Modulus (Tested at 20 Inches/minute) | 4610 | psi |
| 300% Modulus (Tested at 20 Inches/minute) | NA | — |
| Elongation (Tested at 20 Inches/minute) | 300 | % |
| Tensile Strength (Tested at 20 Inches/minute) | min. 6375 | psi |