Hauthane L-3615 is a hard, co-solvent-free, aliphatic polyester polyurethane dispersion.
Identification
- CASE Ingredients Functions
- Binder & Resin
Product families
Applications
- Metal Coatings
Product Families
- Polyurethanes (PU)
Other characteristics
- Brand
- Hauthane
- End Uses
- Top Coat
- Features
Abrasion Resistance, Chemical Resistance, Excellent Adhesion, Excellent Stability, Good Toughness, Improved Flexibility, Low Temperature Flexibility, Water Resistance
- Compatible Substrates & Surfaces
- Concrete, Metal, Plastics, Wood
- Curing
Hauthane L-3615 can be air dried, if desired, depending on film thickness.. Typical drying temperatures and dwell times for aqueous coatings are sufficient to produce optimal film properties.
- Markets
- Paints & Coatings
- Cure
- Air Dry
- Technology
- CASE Ingredients
- Suggested Uses
Hauthane L-3615 was designed for topcoat applications on a wide variety of substrates, including concrete, metal, plastic and wood.; It may also be used as a blending resin with the softer Hauthane L-3614 to impart greater film flexibility.; A balanced composition provides good stability with acrylics and confers superior strength, abrasion resistance and low temperature flexibility properties.
- Labeling Claims
- APEO-Free
- Cosolvent-free
- TEA-free
- Tin-free
- Product Features
- Co-solvent free, TEA free, Tin free, APEO free
- Medium hard, tough, dry film
- Excellent water and chemical resistance
- Superior abrasion resistance
- Good adhesion to a wide variety of substrates
- Application Methods
- Knife-over-roll
- Padding
- Spray
- Applications
Hauthane L-3615 can be used as a sole vehicle or blended with other coatings for spray or pad bath applications.; Solids can be adjusted with water to optimize dry coating weight.; This product may also be thickened with associative thickeners for knife-over-roll or similar methods.
- Coating End Applications
- Top Coat
- Compatible Polymers and Resins
- Acrylics
- Compatible Substrates and Surfaces
- Concrete
- Metal
- Plastics
- Wood
Technical data
Table 1 of 2
6 rows| Characteristic | Value | Unit |
|---|---|---|
| Solid Content | 34 - 36 | % |
| Viscosity | 50 - 500 | cPs |
| pH Value | 7.5 -10.0 | — |
| Density | 8.8 | lbs/gal |
| Softening Point | 360.0 | °F |
| Volatile Organic Compound (less water) | 45.0 | lbs/gal |
Table 2 of 2
4 rows| Characteristic | Value | Unit |
|---|---|---|
| Elongation (Tested at 20 Inches/minute) | 260.0 | % |
| Tensile Strengh (Tested at 20 Inches/minute) | min. 6000 | psi |
| 100% Modulus (Tested at 20 Inches/minute) | 4300.0 | psi |
| 200% Modulus (Tested at 20 Inches/minute) | 5500.0 | psi |