SODOX N°1 353 WELDABLE CONVERSION PRIMER
SODOX N°1 353 WELDABLE CONVERSION PRIMER is a passivating conversion primer forming organo metallic complexes ensuring its weldability. Exists in 3 shades : Pink beige : 353 0101 00 - Gray 353 0200 00 - Black 353 0900 00.
Product families
- Primers & Sealers
Other characteristics
- Brand
- SODOX
- Features
- Good Thermal Stability, Weldable
- Product Type
- Primer, Solventborne Coating
- Primer
- Solventborne Coating
- Application Method
- Gun
- Compatible Substrates & Surfaces
- Aluminum, Iron, Metal, Steel
- Color
- Beige
- Black
- Grey
- Pink
- Steaming
Desolvation 15 minutes at 20°C. Then 30 minutes at 60°C or 15 minutes at 80°C
- PACKAGING
- THINNER 502000700
- 5 L and 20 L
- Shelf LIfe
- THINNER 502000700
- 36 months
- Technology
- Ready-to-Use Products
- Application Methods
Gun; Recommended air pressure; Brush and roller : not recommended - Not adapted to an electrostatic application cleaning thinner : 501 0009 00
- Fonction - Quality
Protection of cold rolled steels to be welded. Applicable after sandblasting, shot blasting or degreasing. Temporary primary 18 months. Thermal resistance continuously from 150 to 350 °C and discontinuously at 650 ° C. Insensitive to water and steam. Adhesion primer on ferrous and non-ferrous metals.
- Paint Préparation
Mix before use then add the suitable thinner under stirring ( linked to the support type to be protected). Make sure that the different constituents (base, thinner) are homogeneous. After thinning, we recommed you to pass the productt hrough a 190 μm filter.
- Viscosity at 20°C
Viscosity range of base + Thinner : 15 to 25 secondes in CA4
- Storage Temperature
- THINNER 502000700
- Surface Preparation
The support must be suitably prepared: degreased and mechanical or chemical prepared. Do not use on greased, contaminated, rusty, damp, condensing or frozen substrates.
- Overcoating Interval
Minimum 60 minutes when dried at air 20°C/ maximum 6 months without grinding. Do not cover with paints containing chlorinated solvents.
- Application Substrates
Ferrous and non-ferrous metals, galvanized steel and aluminum.
- Application Temperature
The temperature of the application cabin, the support and the paint must be between 15 and 30 ° C to obtain an application quality. The substrate temperature must be 3 ° C higher than the dew point temperature. The relative humidity must be less than 65%.
- Pot Life of mixed product
- THINNER 502000700
- Ready to Use Product Features
- Good Thermal Stability
- Weldable
- Compatible Substrates and Surfaces
- Aluminum
- Iron
- Metal
- Steel
Technical data
Table 1 of 1
11 rows| Characteristic | Value | Unit |
|---|---|---|
| Recommanded dry film thickness (On steel ) | 20 - 25 | μm |
| Recommanded dry film thickness ( On aluminium) | 10.0 | μm |
| Maximum film thickness | 25.0 | μm |
| wet film thickness | 155.0 | μm |
| Coverage ( 100% transfer rate ) | 6.5 - 8 | m²/L |
| Dilution for steel substrate (THINNER 502000700) | 15 - 25 | % |
| Dilution for aluminium substrate (THINNER 502000700) | 30.0 | % |
| Specific gravity (BASE 353) | 0.880 - 1.040 | g/cm3 |
| Specific gravity (THINNER 502000700) | 0.795 - 0.815 | g/cm3 |
| Mass solid contained (BASE 353) | 25 - 27 | % |
| Mass solid contained (THINNER 502000700) | Normally Closed | — |