LIOPUR PFL 1284
- CASE Ingredients Functions
- Binder & Resin
- Chemical Family
- Polyurethanes (PU)
LIOPUR PFL 1284 is a aqueous solvent free aliphatic polyurethane dispersion based on a special polyester combination.
Properties
- Physical Form
- Dispersion
Product families
Applications
- Consumer Goods — Furniture; Consumer Goods — Other Consumer Goods Applications; Consumer Goods — Stationery; Art & Office Supplies
- Architectural Coatings
- Wood Coatings & Finishes
- Architectural Coatings
- Craft & Hobby
- Other Consumer Applications
- Wood Flooring
- Furniture Coatings
- Industrial Coatings
Product Families
- Polyurethanes (PU)
Other characteristics
- Brand
- LIOPUR
- End Uses
- 1K (1 component) Coating
- Compatible Substrates & Surfaces
- Wood
- Carrier
- Water
- Markets
- Adhesives & Sealants
- Building & Construction
- Consumer Goods
- Paints & Coatings
- Storage
The dispersion should be stored in tightly closed containers, protected from frost.
- Appearance
- Transparent to Colloidal
- Cure
- Chemical Cure
- Supplied As
- 34% in water
- Coating Type
- 1K (1 component) Coating
- Technology
- CASE Ingredients
- Properties and Fields of use
Liopur PFL 1284 needs an amount of appr 5 % butylglycol for film formation. Coatings based on Liopur PFL 1284 form tack-free, transparent films with very good surface hardness after air drying, high flexibility and elasticity. These coatings exhibit a very good water resistance and good ethanol resistance. Liopur PFL 1284 is suitable for 1C NMP-free wood lacquers in combination with self crosslinking Acrylic emulsions like Liocryl XAM 2851 or Liocryl XAM 2714 resulting in very good chemical resistance according to DIN 68861 1B. These lacquers give good sandability, overcoatability and high pendulum hardness together with good elasticity even at low temperature (cold-check test). Lacquers based on Liopur PFL 1284 and Liocryl XAM 2714 result in good creme resistance and show a good grain enhencement on oak, beech and nut wood. . After drying for 7 days at room temperature, films based on Liopur PFL 1284 have the following properties determined by a Zwick materials test (pre selected force 1N, test rate 100 mm/min): Tear strength approx. 1,5 N/mm² Elongation on break approx. 300 %
- Compatible Substrates and Surfaces
- Wood
Technical data
Table 1 of 1
5 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Viscosity | 20-500 | mPas | AV-F-V005 |
| Minimum Film Forming Temperature | approx. 40 | °C | — |
| Non Volatile Content | 342 | w % | AV-F-F003 |
| Organic solvent | Max. 0.5 | — | — |
| pH-value | 7.0-9.0 | — | AV-F-P001 |