LIOPUR PFL 2392
- CASE Ingredients Functions
- Binder & Resin
LIOPUR PFL 2392 is a aqueous, aliphatic modified polyurethane dispersion based on a polyester, solvent free and triethylaminfree, free of surfactants.
Properties
- Physical Form
- Dispersion
Identification
Product families
Applications
- Consumer Goods — Furniture; Consumer Goods — Other Consumer Goods Applications; Consumer Goods — Stationery; Art & Office Supplies
- Automotive OEM Coatings
- Architectural Coatings
- Wood Coatings & Finishes
- Architectural Coatings
- Automotive OEM Coatings
- Craft & Hobby
- Other Consumer Applications
- Wood Flooring
- Furniture Coatings
- Industrial Coatings
- Metal Coatings
Product Families
- Polyurethanes (PU)
Other characteristics
- Brand
- LIOPUR
- End Uses
1K (1 component) Coating, 2K (2 component) Coating
- Compatible Substrates & Surfaces
- Metal, Plastics, Wood
- Usage
After air-drying film coatings based on Liopur PFL 2392 form transparent films which are tackfree and display good surface resistance of appr. 50 sec Pendulum hardness after König (90 μm wet film after 24 h drying at room temperature). Liopur PFL 2392 exhibits good flexibility and elasticity Liopur PFL 2392 is designed for waterbased 1C basecoats with good humidity resistance and good adhesion to different plastics due to the hydrophobic polymer character and its good intercoat adhesion to conventional 2C topcoats After drying for 7 days at room temperature, films based on Liopur PFL 2392 have the following properties determined by a Zwick materials test (pre selected force 1N, test rate 100 mm/min): Tear strength approx. 10 N/mm² Elongation on break approx. 200 %
- Carrier
- Water
- Markets
- Adhesives & Sealants
- Automotive & Transportation
- Building & Construction
- Consumer Goods
- Paints & Coatings
- Storage
At 23°C its shelf life is at least 6 months. No la belling is required under the German Dangerous Substances Directive.
- Appearance
- Colloidal to Milky
- Cure
- Chemical Cure
- Supplied As
- 40 % in water
- Coating Type
- 1K (1 component) Coating
- 2K (2 component) Coating
- Technology
- CASE Ingredients
- Labeling Claims
- TEA-free
- Compatible Substrates and Surfaces
- Metal
- Plastics
- Wood
Technical data
Table 1 of 1
5 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Viscosity | 20-400 | mPas | AV-F-V005 |
| Minimum Film Forming Temperature | Max. 20 | °C | — |
| Non Volatile Content | 40 2 | w % | AV-F-F003 |
| Organic solvent | 0 | — | — |
| pH-value | 7.0-9.0 | — | AV-F-P001 |