Plastazote® LD45
- Chemical Family
- Polyethylenes, PolyolefinsPolyethylenesPolyolefins
Plastazote® LD45 is a closed cell, cross-linked polyethylene block foam manufactured using Zotefoams unique production process.
Product families
Automotive & Transportation — Automotive
- Interior
- Powertrain & UTH
Printing & Packaging — Packaging
- Industrial & Transport Packaging
Other characteristics
- Brand
- C.B.Frost & Co. Plastazote
- End Uses
- Gaskets
- Foam Type
- Closed Cell Foam
- Color
- Black
- Blue
- Red
- White
- Markets
- Automotive & Transportation
- Printing & Packaging
- Polymer Name
- Low Density Polyethylene (LDPE)
- Product Type
- Foam
- Technology
- Ready-to-Use Products
- Product Families
- Ready-to-Use Products — Foams
- Ready to Use Product Features
- Excellent Seal Properties
- Vibration Damping
- Recommended Maximum Operating Temperature
The maximum operating temperature shown is defined as the temperature which will typically cause a linear shrinkage of 5% after a 24 hour exposure period, using sample dimensions of 100mm x 100mm x 25mm. This figure is provided for general guidance only. The actual level of shrinkage the foam will undergo at any particular temperature is dependent on a number of system variables such as, sample dimensions, cell size, loading conditions and exposure period.
Technical data
Table 1 of 1
14 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Density (Skin) | 45.0 | Kg/m³ | BS EN ISO 7214:2012 |
| Cell Size (Cell Diameter) | 0.4 | mm | Internal |
| Compression Stress (Strain, 25% compression, 25mm cell) | 90.0 | kPa | BS EN ISO 7214:2012 |
| Compression Stress (Strain, 50% compression, 25mm cell) | 163.0 | kPa | BS EN ISO 7214:2012 |
| Tensile Strength | 537.0 | kPa | BS EN ISO 7214:2012 |
| Tensile Elongation | 155.0 | % | BS EN ISO 7214:2012 |
| Compression Set (25% comp., 22hr, 23°C, 1⁄2 hr recovery, 25mm cell) | 8.0 | % set | BS EN ISO 7214:2012 |
| Compression Set (25% comp., 22hr, 23°C, 24 hr recovery, 25mm cell) | 3.0 | % set | BS EN ISO 7214:2012 |
| Tear Strength | 2414.0 | N/m | BS EN ISO 8067:2008 Method B |
| Hardness | 63.0 | Shore 00 | BS EN ISO 868:2003 |
| Recommended maximum operating temperature | 100.0 | °C | Internal |
| Flammability (Automotive) | Pass at 6mm | max. 100mm/min. | FMVSS.302 – Burn Rate |