Polifil® GFRMPPCC-40
- Chemical Family
- PolyolefinsPolypropylenes (PP)
Polifil® GFRMPPCC-40 are high impact polypropylenes reinforced with chemically coupled glass fibers. This combination provides higher impact strength while retaining high stiffness. These compounds are used in appliances, electrical components, automotive and utility products. Standard processing techniques are applicable. Use this information as a guide to aid you in selecting the proper resin for your application. TPG will custom compound and fine-tune our formulations for your application.
Properties
- Physical Form
- Pellets
- Solid
Product families
Applications
Applications
- Consumer Goods — Appliances & Electronics; Consumer Goods — Other Consumer Goods Applications
Automotive & Transportation — Automotive
- Other Automotive Applications
Electrical & Electronics — Devices & Assemblies
- Consumer Electronics
Electrical & Electronics — Parts & Components
- Other Parts & Components
Product Families
Plastics — Basic Thermoplastics
- Polyolefins
Other characteristics
- Brand
- Polifil
- Polymer Name
- Polypropylene (unspecified)
- Melt Flow Index
- 4.0 - 10.0 g/10 min
- Fillers Included
- Glass Fiber
- Markets
- Automotive & Transportation
- Consumer Goods
- Electrical & Electronics
- Technology
- Plastics
- Material Features
- Chemically Coupled
- Good Impact Strength
- High Stiffness
- Chemical Inventories
- TSCA (USA)
- Usage
Use this information as a guide to aid you in selecting the proper resin for your application. TPG will custom compound and fine-tune our formulations for your application.
- Certifications and Compliance
- REACH (Europe)
- RoHS 2 Compliant
- RoHS 3 Compliant
- RoHS Compliant
- Plastics and Elastomers End Uses
- Appliances
- Electrical Components
- Plastics and Elastomers Functions
- Resin
Technical data
Table 1 of 3
5 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Reinforcement content | 40 | — | TPG WI |
| Specific gravity | 1.22 | — | D 792 |
| Melt flow 230/2.16 | 4-10 | g/10 min | D 1238 |
| Water absorption, 24 hours | nil | % | D 570 |
| Mold shrinkage – 1/8˝ specimen | 0.003 | in/in | D 955 |
Table 2 of 3
9 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Rockwell hardness | 96 | Scale R | D 785 |
| Tensile strength | 12500 | psi | D 638 |
| Tensile modulus | 580 | kpsi | D 638 |
| Flexural modulus, tangent | 700 | kpsi | D 790 |
| Flexural strength | 14000 | psi | D 790 |
| Izod impact, notched | 3 | ft-lbs/in | D 256 |
| Gardner impact, 1/2˝ tup | 6 | in-lbs | D 5420 |
| Elongation (Break) | 3 | % | D 638 |
| Elongation (Yield) | 3 | % | D 638 |
Table 3 of 3
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Deflection temperature, 66psi | 305 | ˚F | D 648 |
| Deflection temperature, 264psi | 295 | ˚F | D 648 |