Fine-Blend PP-g-MAH CMG5701
- Chemical Family
- Polyolefins
Fine-Blend PP-g-MAH CMG5701 is a low odor and TVOC maleic anhydride modified polypropylene recommended for long fiber reinforced polypropylene (LFT-PP) modification. It has high graft ratio and great high temperature stability in processing.
Product families
- Polyolefins
Other characteristics
- Polymer Name
Maleic Anhydride Grafted Polypropylene (MAH-g-PP)
- Processing Methods
- Extrusion
- Markets
- Automotive & Transportation
- Building & Construction
- Consumer Goods
- Electrical & Electronics
- Applications
Automotive & Transportation — Other Automotive & Transportation Applications; Building & Construction — Other Building & Construction Applications; Consumer Goods — Other Consumer Goods Applications; Electrical & Electronics — Other Electrical & Electronics Applications
- Technology
- Plastics
- Material Features
- Good Adhesion
- Low Odor
- Processing Information
Fine-Blend® CMG5701 can be processed over a wide range of conditions. The typical processing temperature range is from 200℃ to 300℃, and it is related to the type of extruder, screw design, screw speed, yield and the residence time etc
- Certifications and Compliance
- RoHS Compliant
- Storage, Handling and Safety
Fine-Blend® CMG5701 should be stored in dry conditions protect from high temperature and UV-light. Improper storage conditions may cause degradation and have consequences on physical properties of the product
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Extrusion
Technical data
Table 1 of 1
4 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Weight loss | max. 0.3 | wt% | 105℃，10min |
| Density | 0.90-0.92 | g/cm3 | ASTM D792 |
| Graft level | Very high | — | Acid-base titration1 |
| MFR(190℃/2.16kg) | 50-100 | g/10min | ASTM D1238 |