Norplex-Micarta BR70
- Chemical Family
- Phenols & Phenolics
BR70 is a red colored composite made from a 24 oz/sq. yd canvas which is passed through the treater twice to insure impregnation of the fibers and to obtain the resin content desired for optimal performance. The resin system is a phenolic with good impregnation qualities and cured hardness. BR70 is designed for highly loaded bearing applications, where the lubrication is provided by oil, water or a mixture.
Properties
- Physical Form
- Sheets
Product families
Applications
Industrial — Chemical & Industrial Manufacturing
- Equipment & Parts
Automotive & Transportation — Transportation
- Marine
Product Families
Composite Materials — Prepregs & Molding Compounds
- Laminates
Other characteristics
- End Uses
- Marine Applications
- Functions
- Laminate
- Polymer Name
- Phenolic Compound
- Reinforcement Material
- Cotton
- Note
1 This temperature is a recommendation only, and based upon experience in various applications. The maximum operating temperature is dependent upon the application and should be investigated prior to use.. *t₁= Thickness tested at 0.500 inch
- Markets
- Automotive & Transportation
- Industrial
- Technology
- Composite Materials
- Composites End Use
- Marine Applications
- Material Features
- Bearing Grade
- Consistent Performance
- Excellent Lubricity
- High Hardness
- Composite Materials Functions
- Laminate
Technical data
Table 1 of 2
15 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Bonding Strength (Condition A, *t₁) | 1043.3 | kg | ASTM D229 |
| Bonding Strength (Condition D-48/50, *t₁) | 952.5 | kg | ASTM D229 |
| Compressive Strength (Condition A, Flatwise, *t₁) | 251.7 | Mpa | ASTM D695 |
| Flexural Modulus (Conditon A, Crosswise, *t₁) | 7.1 | Gpa | ASTM D790 |
| Flexural Modulus (Conditon A, Lengthwise, *t₁) | 9.4 | Gpa | ASTM D790 |
| Flexural Strength (Conditon A, Crosswise, *t₁) | 93.8 | Mpa | ASTM D790 |
| Flexural Strength (Conditon A, Lengthwise, *t₁) | 139.3 | Mpa | ASTM D790 |
| Izod Impact Strength (Condition E-48/50, Crosswise, *t₁) | 1.51 | J/cm | ASTM D256 |
| Izod Impact Strength (Condition E-48/50, Lengthwise,*t₁) | 3.39 | J/cm | ASTM D256 |
| Moisture Absorption (Condition A, *t₁) | 0.06 | % | ASTM D570 |
| Rockwell Hardness (0.250" Build-up, *t₁) | 95 | M Scale | ASTM D785 |
| Shear Strength (Condition A, Perpendicular, *t₁) | 95.8 | Mpa | ASTM D732 |
Table 2 of 2
4 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Coefficient of Thermal Expansion (X-axis, *t₁) | 19.5 x10⁻⁶ | in/in/°C | IPC-TM 650-2.4.24 |
| Coefficient of Thermal Expansion (Y-axis, *t₁) | 27.6 x10⁻⁶ | in/in/°C | IPC-TM 650-2.4.24 |
| Flammability Rating (Condition A, *t₁) | HB | Class | UL Bulletin 94 |
| Temperature Index¹ (Mechanical, *t₁) | 125 | °C | UL Bulletin 746b |