SYNTHALAT A 150
- CASE Ingredients Features
- Abrasion ResistanceChemical Resistance
- Chemical Family
- Acrylics & Acrylates
SYNTHALAT A 150 is a polyisocyanate-curing acrylic resin.
Identification
- CASE Ingredients Functions
- Binder & Resin
Product families
- Acrylics
Other characteristics
- Brand
- SYNTHALAT
- End Uses
- 2K (2 component) Coating, Top Coat
- Features
- Abrasion Resistance, Chemical Resistance
- Compatible Substrates & Surfaces
- Metal
- Usage
2-pack coatings which are air- and oven-drying in combination with aliphatic polyisocyanates, for industrial coatings affording high mechanical strength, good adhesion and resistance to weathering.
- Carrier
- Solvent-based
- Markets
- Automotive & Transportation
- Paints & Coatings
- Cure
- Chemical Cure
- Supplied As
A = 60% in xylene/shellsol A/ butyl acetate (2:1:1) B = 60% in butyl acetat
- Coating Type
- 2K (2 component) Coating
- Top Coat
- Pigmentation
SYNTHALAT-A 150 has high pigment absorption and very good pigment wetting properties. Any neutral pigments or fillers are suitable for pigmentation. Basic pigments and pigments containing soluble metal compounds may have a catalytic effect on curing and shorten the pot life of coating batches once mixed.
- Technology
- CASE Ingredients
- Film Properties
In combination with aliphatic polyisocyanates such as "Desmodur N" they afford non-yellowing finishes with excellent weather resistance and gloss retention. Such films have good resistance to scratching and abrasion, combined with good solvent resistance. Their good resistance to water and aggressive chemicals should also be emphasized. SYNTHALAT-A 150 differs from A 045, A 055, A 065 and A 085 in its higher cross-linking density, which affords films having significantly greater abrasion and solvent resistance. These values are exceeded only by A 190 with its higher cross-linking density.
- Properties and Fields of use
The main field of application for SYNTHALAT-A 150 is in coatings for metals and plastics which are air- and oven-drying in combination with aliphatic polyisocyanates. This type of 2-pack coating is preferred where the size or temperature sensitivity of objects to be coated stands in the way of achieving the required high-grade coating qualities. Examples are car refinishing, original finishing of busses and trams, plastic items, etc.
- Compatible Substrates and Surfaces
- Metal
Technical data
Table 1 of 1
7 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Non Volatile Content | Max. 2 | w % | AV-F-F003 |
| Density | 0.99 | g/ml | AV-F-0D001 |
| Flash point | 30 | °C | AV-F-f006 |
| Flash point | 60 | °C | AV-F-f006 |
| Flow Time | 140-180 | sec | AV-F-V003 |
| Hydroxyl Content | 4.5 | % | Relative to NVC |
| Hydroxyl Content | 130-150 | % | Relative to NVC |