CORAPACK BRi 13
- Chemical Family
- PolyethylenesPolyolefins
Corapack BRi 13 contains 30% of post-industrial regenerated raw material. Contributes to carbon sequestration through participation in a carbon-sink forestry project. It is perfectly adapted for the packaging of industrial and consumer goods. Ultrathin display shrinkfilm on the basis of bi-oriented polyethylene (BO-PE) and recycled raw material.
Properties
- Physical Form
- Film
Product families
- Food & Beverage Packaging
- Industrial & Transport Packaging
- Non-Food Consumer Packaging
Other characteristics
- Features
Compostable, Food Contact Acceptable, High Cohesion, Highly Versatile, Thin Wall Thickness; Versatility; High cohesion strength; Extremely thin, thus contributing to resource savings; Recyclable
- Polymer Name
- Polyethylene (unspecified)
- Markets
- Printing & Packaging
- Disposal
Options for disposal are recycling (compatible with SPI code 4/PE-LD), incineration with energy recovery and landfill. Treatment, storage, transportation, and disposal must be in accordance with applicable federal, state/provincial and local regulations.
- Film Storage
The maximum temperature for storage is 32°C, with a maximum of 80% RH, up to one year.
- Food Contact
Complies with EU and US regulations on food contact materials.
- Presentation
- mini
- 150 - maxi : 1 400 - increment : 5
- mini
- 150 - maxi : 1000 - increment : 50
- Technology
- Plastics
- Labeling Claims
- Contains PIR Resin
- Food Contact Acceptable
- Recyclable
- Recycled
- Product Families
- Plastics — Parts, Shapes & Films
- Material Features
- Compostable
- Food Contact Acceptable
- High Cohesion
- Highly Versatile
- Thin Wall Thickness
- Plastics and Elastomers End Uses
- Film
- Shrink Wrap
Technical data
Table 1 of 5
6 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Elongation at Break (Longitudinal Direction) | 67.0 | % | ASTM D882 |
| Elongation at Break (Transversal Direction) | 90.0 | % | ASTM D882 |
| Stiffness Modulus (Longitudinal Direction) | 650.0 | Mpa | ASTM D882 |
| Stiffness Modulus (Transversal Direction) | 750.0 | Mpa | ASTM D882 |
| Tensile Strength (Longitudinal Direction) | 1000.0 | Kg/cm² | ASTM D882 |
| Tensile Strength (Transversal Direction) | 1000.0 | Kg/cm² | ASTM D882 |
Table 2 of 5
2 rows| Characteristic | Value | Method |
|---|---|---|
| Friction Coefficients Dynamic (Film to Film) | 0.18 | ASTM D1894 |
| Friction Coefficients Static (Film to Film) | 0.37 | ASTM D1894 |
Table 3 of 5
6 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Free Shrink at 120° (Longitudinal Direction) | 59.0 | % | ASTM D2732 |
| Free Shrink at 120° (Transversal Direction) | 58.0 | % | ASTM D2732 |
| Free Shrink at 93° (Longitudinal Direction) | 17.0 | % | ASTM D2732 |
| Free Shrink at 93° (Transversal Direction) | 17.0 | % | ASTM D2732 |
| Shrink Force (Longitudinal Direction) | 27.0 | Kg/cm² | NFT 54-125 |
| Shrink Force (Transversal Direction) | 28.0 | Kg/cm² | NFT 54-125 |
Table 4 of 5
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Gloss at 20° | 90.0 | — | ASTM D2457 |
| Haze | 5.0 | % | ASTM D1003-A |
Table 5 of 5
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Oxygen Transmission Rate (23°C, 0% HR) | 9400.0 | cm³/m²/24h | ASTM D3985 |
| Water Vapor Transmission Rate (38°C, 95% HR) | 21.0 | g/m²/24h | ASTM E96 |