B-Nat®O 15 is an ultrathin packaging shrink film developed on a basis of green polyethylene. It consists for more than 40% of a polyethylene produced from sugarcane ethanol. Besides coming from a renewable natural source, this green PE provides the same performances as a fossil polyethylene, can be recycled and contributes to minimizing the carbon footprint. Ultrathin display shrinkfilm on the basis of a green polyethylene standard multipurpose.
Properties
- Physical Form
- Film
Product families
- Food & Beverage Packaging
- Non-Food Consumer Packaging
Other characteristics
- Brand
- B-Nat
- Features
Compostable, Food Contact Acceptable, Good Cohesion, Good Optical Properties, Recyclable, Renewable Resource Content; B-Nat® O is developed to offer the most attractive shelf presentation. Therefore, its optic properties are optimized.; Its cohesion strength makes it a good candidate for multipacking applications.; The unique technical properties of B-Nat® O ensure excellent results, from manual to automatic high speed machines.
- Polymer Name
- Polyethylene (unspecified)
- Markets
- Printing & Packaging
- Disposal
Options for disposal are recycling (compatible with SPI code 4/PE-LD), incineration with energy recovery and landfill. Treatment, storage, transportation, and disposal must be in accordance with applicable federal, state/provincial and local regulations.
- Film Storage
The maximum temperature for storage is 32°C, with a maximum of 80% RH, up to one year.
- Food Contact
Complies with EU and US regulations on food contact materials.
- Presentation
- mini
- 150 - maxi : 1 400 - increment : 5
- mini
- 150 - maxi : 700 - increment : 50
- Technology
- Plastics
- Labeling Claims
- Food Contact Acceptable
- Low Carbon Footprint (PCF)
- Product Families
- Plastics — Parts, Shapes & Films
- Material Features
- Compostable
- Food Contact Acceptable
- Good Cohesion
- Good Optical Properties
- Recyclable
- Renewable Resource Content
- Plastics and Elastomers End Uses
- Film
- Shrink Wrap
Technical data
Table 1 of 5
6 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Elongation at Break (Longitudinal Direction) | 90.0 | % | ASTM D882 |
| Elongation at Break (Transversal Direction) | 100.0 | % | ASTM D882 |
| Stiffness Modulus (Longitudinal Direction) | 500.0 | Mpa | ASTM D882 |
| Stiffness Modulus (Transversal Direction) | 600.0 | Mpa | ASTM D882 |
| Tensile Strength (Longitudinal Direction) | 1000.0 | Kg/cm² | ASTM D882 |
| Tensile Strength (Transversal Direction) | 1100.0 | Kg/cm² | ASTM D882 |
Table 2 of 5
2 rows| Characteristic | Value | Method |
|---|---|---|
| Friction Coefficients Dynamic (Film to Film) | 0.12 | ASTM D1894 |
| Friction Coefficients Static (Film to Film) | 0.4 | ASTM D1894 |
Table 3 of 5
6 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Free Shrink at 120° (Longitudinal Direction) | 58.0 | % | ASTM D2732 |
| Free Shrink at 120° (Transversal Direction) | 60.0 | % | ASTM D2732 |
| Free Shrink at 93° (Longitudinal Direction) | 15.0 | % | ASTM D2732 |
| Free Shrink at 93° (Transversal Direction) | 20.0 | % | ASTM D2732 |
| Shrink Force (Longitudinal Direction) | 22.0 | Kg/cm² | NFT 54-125 |
| Shrink Force (Transversal Direction) | 28.0 | Kg/cm² | NFT 54-125 |
Table 4 of 5
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Gloss at 20° | 114.0 | — | ASTM D2457 |
| Haze | 3.0 | % | ASTM D1003-A |
Table 5 of 5
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Oxygen Transmission Rate (23°C, 0% HR) | 8000.0 | cm³/m²/24h | ASTM D3985 |
| Water Vapor Transmission Rate (38°C, 95% HR) | 19.0 | g/m²/24h | ASTM E96 |