Isodur® A 15 10 GF30

Chemical Family: Polyesters

Isodur® A 15 10 GF30 is compound based on different Polyesters and special alloys with wide viscosity range. The products are usually glass fiber reinforced, impact modified, UV stabilized and colored upon specific customer requirement. Availability of flame retardant grades with registered UL certification.

Product families

Applications

Industrial — Chemical & Industrial Manufacturing

Tooling & Moldmaking

Product Families

Plastics — Engineering & Specialty Polymers

Polyesters & Copolyesters

Other characteristics

Brand: Isodur
Polymer Name: Polybutylene Terephthalate (PBT)
Fillers Included: Glass Fiber
Flexural Modulus: 8500.0 - 8500.0 MPa
Processing Methods: Injection Molding
Markets: Industrial
Application: Knobs, electric components, connectors, air fan, lamp holder.
Flame Rating: UL 94 HB
Technology: Plastics
Certifications and Compliance: RoHS Compliant
UL 94
Plastics and Elastomers End Uses: Mold Making
Plastics and Elastomers Functions: Resin
Plastics and Elastomers Processing Methods: Injection Molding

Technical data

Table 1 of 3

5 rows

Characteristic	Value	Unit	Method
Flexural Modulus (23°C - 2 mm/min)	8500	MPa	ISO 178
Tensile stress at break (23°C-5 mm/min)	125	MPa	ISO 527-2
Tensile elong. at break (23°C-5 mm/min)	2,0	%	ISO 527-2
Izod notched impact strength (23°C)	8	KJ/m²	ISO 180/1A
Charpy unnotched impact strength (23°C)	55	KJ/m²	ISO 179/1eU

Table 2 of 3

8 rows

Characteristic	Value	Unit	Method
Melt Flow Rate (250°C – 2,16 Kg)	15	g/10'	ISO 1133
Density at 23°C	1,56	g/cm3	ISO 1183
Mould Shrinkage	0,4-0,6	%	INTERNAL
Filler Content (1h/600°C)	30	%	ISO 3451-1
Melt Temperature Range	240-260	°C	ISO 294
Mold Temperature Range	80-100	°C	ISO 294
Injection Velocity	MEDIUM	—	ISO 294
Drying Time	3	Hour	—

Table 3 of 3

2 rows

Characteristic	Value	Unit	Method
Vicat B50	210	°C	ISO 306
HDT, A (1.80 MPa)	205	°C	ISO 75/Af