C-POXY 15
- Chemical Family
- Epoxy & Epoxy Derivatives
C-POXY 15 is a general-purpose, unfilled, fast-setting epoxy adhesive. Recommended for bonding metal, ceramics, stone, glass, concrete, wood, fiberglass and many plastics such as polyester, ABS and rigid PVC (not suitable for PTFE-PP-PE and rubbers).
Product families
Applications
- Body Shop & Repair
- Repair Adhesives
Product Families
- Structural Adhesives
Other characteristics
- Brand
- C-POXY
- Product Type
- Epoxy Adhesive
- Compatible Substrates & Surfaces
Acrylonitrile Butadiene Styrene (ABS), Ceramic, Concrete, Fiberglass, Glass, Metal, Plastics, Polyesters, Polyvinyl Chloride (PVC), Stone, Wood
- Markets
- Adhesives & Sealants
- Automotive & Transportation
- Storage
Product must be kept in a cool and dry room at 10°C to 25°C.
- Shelf LIfe
Minimum two years in unopened packaging at +5°C/+27°C.
- Technology
- Ready-to-Use Products
- Use Direction
Part A and B need to be mixed thoroughly in the correct volume ratio for minimum 1 minute before use. Gel time of the mixed product is 14 – 16 minutes at room temperature.; Parts requiring bonding should be assembled and kept close without any stress. Assembling is continued until full curing takes place.; Excess of the product can be cleaned with Acetone or any solvent-based cleaner compatible with the substrates to bond.; For best results, it is recommended to scratch (if possible) the surface, then gently degrease and clean the excess material off the area.; NOTE: Shear strength will increase roughly to 25 – 27 N/mm² if bonding parts are allowed to cure 50 minutes at room temperature 25°C (77°F) followed by 2 hours cure at 100°C (212°F) (if possible).
- Common Applications
- Model construction
- Toy repairs
- Ceramic repairs
- Furniture repair/manufacturing
- Jewelry repair/manufacturing
- Pen manufacturing
- Knife making
- Woodworking
- Ready to Use Product Features
- Fast Setting
- General Purpose
- Compatible Substrates and Surfaces
- Acrylonitrile Butadiene Styrene (ABS)
- Ceramic
- Concrete
- Fiberglass
- Glass
- Metal
- Plastics
- Polyesters
Technical data
Table 1 of 2
8 rows| Characteristic | Value |
|---|---|
| Composition (Part A, Resin) | Epoxy Resin |
| Viscosity (Part A, Resin, 25°C) | 11000 - 13000 |
| Specific Gravity (Part A, Resin, 25°C) | 1.19 |
| Mixing Ratio (Part A, Resin, Volume) | 1.0 |
| Composition (Part B, Hardener | Polymercaptan |
| Viscosity (Part B, Hardener, 25°C) | 12000 - 14000 |
| Specific Gravity (Part B, Hardener, 25°C) | 1.12 |
| Mixing Ratio (Part B, Hardener, Volume) | 1.0 |
Table 2 of 2
6 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Pot Life (Time Detected using 6g Total Mass) | 14 - 16 | min | — |
| Cure Time (Functional) | 1.0 - 2.0 | hours | — |
| Mixing Colour | Colorless/Clear | — | — |
| Shear Strength | 11.0 - 15.0 | N/mm² | ISO 4587 |
| Hardness | 75 - 80 | Shore D | — |
| Gap to Fill | 0.1 - 2.1 | mm | — |