Zhejiang Fenghong New Material Polyester BS-1C-3
- CASE Ingredients Features
- Anti-SettlingExcellent Dispersibility
- Chemical Family
- Bentonite
BS-1C-3 is an organic derivative of bentonite clay. This Rheology Modifier is designed for medium polarity organic solvent system, such as toluene and xylene.
Properties
- Physical Form
- Powder, Solid
- Powder
- Solid
Identification
- CASE Ingredients Functions
- Rheology ModifierThickener
Product families
Applications
- Paints & Coatings — Other Paints & Coatings Applications
- Primers & Lacquers
- Primers & Lacquers
Product Families
- Rheology Modifiers & Stabilizers
Other characteristics
- Functions
- Rheology Modifier, Thickener
- Compatible Polymers & Resins
Polyesters, Polyethylenes (PE), Polyurethanes (PU)
- Markets
- Paints & Coatings
- Printing & Packaging
- Storage
Product should be stored in ventilated, cool, and dry place.; Storage life: two years when the temperature is 0~30℃
- PACKAGING
- The package
- kraft complex g bag interior with PE
- The weight
- 25±0.25kg per bag
- The package and weight can be customized
- Appearance
- Off-white/light yellow finely divided powder
- Composition
- Organic derivative of a bentonite clay
- Instructions
BS-1C-3 additive is easy-to-disperse, self-activated organoclay,it does not require achemical (polar) activator to reach the proper level of delamination of theorganoclay platelet stacks.; LEVELS OF USE; The amount of BS-1C-3 Rheology Modifier required depends upon the type of; organic system and the degree of thickening or other properties desired.; Addition levels are typically between 0.5%-2.0% by weight of the total system
- Technology
- CASE Ingredients
- Packaging Type
- Bags
- Compatible Polymers and Resins
- Polyesters
- Polyethylenes (PE)
- Polyurethanes (PU)
Technical data
Table 1 of 1
5 rows| Characteristic | Value | Unit |
|---|---|---|
| Bulk Density | max. 440 | kg/m3 |
| Density | 1.8 | g/cm3 |
| Fineness（-200Mesh） | min. 95.0 | — |
| Loss On Ignition (900℃) | 30.0-34.0 | % |
| Moisture Content | max. 3.00 | % |