Cardolite® NX - 9005
- Chemical Family
- Polyols
Cardolite® NX - 9005 is a unique polyol suitable for polyurethane coatings and adhesives, offering balanced mechanical properties, high tensile strength, and excellent elongation.
Properties
- Physical Form
- Liquid
Product families
CASE Ingredients — Additives
- Functional Additives
Other characteristics
- Brand
- Cardolite
- End Uses
2K (2 Component) Adhesive, Polyurethane Coating, Potting Compound
- Features
Acid Resistance, Alkali Resistance, Chemical Resistance, Excellent Adhesion, Good Elongation, Good Mechanical Properties, High Tensile Strength, Hydrolytic Stability, Improved Flexibility, Improved Hardness, UV Resistance
- Functions
- Curing Agent
- Compatible Polymers & Resins
- Polyurethanes (PU)
- Markets
- Building & Construction
- Paints & Coatings
- Appearance
- Yellow liquid
- Technology
- CASE Ingredients
Technical data
Table 1 of 5
5 rows| Characteristic | Value | Unit |
|---|---|---|
| Tensile Strength | 17.6 | MPa |
| Hardness | 72.0 | Shore D |
| Lap Shear Strength (Blasted steel furnace) | 11.2 | MPa |
| Elongation At Break | 83.0 | % |
| Glass Transition Temperature | 24.5 | °C |
Table 2 of 5
9 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Color | max. 5 | Gardner | ASTM D1544 |
| Viscosity (at 25°C) | 2,600 - 4,000 | cPs | ASTM D2196 |
| Hydroxyl Value | 145 - 195 | mg KOH/g | ASTM D1957 |
| Moisture Content | max. 0.15 | % | Karl Fischer |
| Density (at 25°C) | 8.327 | lbs/gal | ASTM D1475 |
| Flash Point | min. 100 | °C | ASTM D93 |
| Hydroxyl Equivalent Weight | 288 - 387 | g/mole | Calculated |
| Bio Content (Calculated) | 79.0 | % | — |
| Average Functionality | 3.2 | — | — |
Table 3 of 5
3 rows| Characteristic | Value | Unit |
|---|---|---|
| Lap Shear Strength Control Sample | 9.3 | MPa |
| Lap Shear Strength (after 80°C/7days water immersion) | 7.1 | MPa |
| Reduction in Lap Shear Strength | 24.7 | % |
Table 4 of 5
7 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Thin Film Dry Times 8 Mils (at 5°C, at 200 micron, hard) | 8.5 | hours | ASTM D5895 |
| Thin Film Dry Times 8 Mils (at 5°C, at 200 micron, through) | 14 | hours | ASTM D5895 |
| MRS - 5 (Poly MDI; NCO eq. Wt 132.1) | 40.3 | — | — |
| Cardolite NX-9005 Content | 100.0 | pbw | — |
| Gel Time (at 25°C, 50 g) | 52.0 | minutes | NTM-15 |
| Hard Dry (at 25°C) | max. 4.5 | hours | — |
| Hard Dry (at 5°C) | max. 18 | hours | — |
Table 5 of 5
1 row| Characteristic | Value | Unit |
|---|---|---|
| CO₂ Polymeric MDI (after 24hr) | 16.0 | ml |