To catalogue
Cardolite® NX - 2003D
- CASE Ingredients Features
- Chemical ResistanceCost EffectiveExcellent AdhesionFast CureHigh PerformanceLow Viscosity
- Chemical Family
- Phenalkamines
Cardolite® NX - 2003D offers fast cure, good adhesion, high surface tolerance, and high chemical resistance.
Identification
- CASE Ingredients Functions
- Curing Agent
Product families
Applications
Paints & Coatings — Automotive & Transportation
- Marine Coatings
Adhesives & Sealants — Building & Construction
- Construction Adhesives
Paints & Coatings — Building & Construction
- Concrete Coatings & Stains
- Floor Coatings
Automotive & Transportation — Coatings & Finishes
- Marine Coatings
Building & Construction — Flooring & Surfaces
- Floor Coatings
Paints & Coatings — Industrial Coatings
- Industrial Coatings
Paints & Coatings — Packaging Coatings
- Primers & Lacquers
Automotive & Transportation — Transportation
- Marine
Product Families
CASE Ingredients — Additives
- Functional Additives
Other characteristics
- Brand
- Cardolite
- End Uses
- 2K (2 Component) Adhesive, Primer
- Features
Chemical Resistance, Cost Effective, Excellent Adhesion, Fast Cure, High Performance, Low Viscosity
- Functions
- Curing Agent
- Labeling Claims
- Solvent-free
- Compatible Polymers & Resins
- Epoxies (EP)
- Note
*Test specimen cured at 40°C for 16 hours with liquid epoxy (EEW 190)
- Markets
- Adhesives & Sealants
- Automotive & Transportation
- Building & Construction
- Paints & Coatings
- Appearance
- Yellow brown
- Technology
- CASE Ingredients
- Product Features
- Fast cure
- Excellent adhesion
- Solvent free
- Coating End Applications
- Primer
- Compatible Polymers and Resins
- Epoxies (EP)
- Compatible Substrates and Surfaces
- Concrete
- Adhesives And Sealants
- 2K (2 Component) Adhesive
Technical data
Table 1 of 2
6 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Glass Transition Temperature | 79.0 | °C | DSC |
| Tensile Strength | 51.0 | MPa | — |
| Flexural Strength | 108.0 | MPa | — |
| Compressive Strength | 75.0 | MPa | — |
| Elastic Modulus | 2309.0 | MPa | — |
| Lap Shear Strength (Sand blasted substrate)* | 20.0 | MPa | — |
Table 2 of 2
12 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Viscosity (at 25°C) | 700.0 | cPs | ASTM D2196 |
| Technology | Phenalkamine | — | — |
| Color | 13.0 | Gardner | ASTM D1544 |
| Amine Value | 357.0 | mg KOH/g | ASTM D2074 |
| Theoretical Active Hydrogen Equivalent (based on total product weight) | 270.0 | — | — |
| Gel Time (at 25°C, 50 g) | 25.0 | minutes | — |
| Thin Film Dry Hard Time (at 25°C, at 200 micron) | 4.5 | hours | ASTM D5895 |
| Thin Film Dry Hard Time (at 5°C, at 200 micron) | 15.0 | hours | ASTM D5895 |
| Thin Film Dry Hard Time (at 0°C, at 200 micron) | 24.0 | hours | ASTM D5895 |
| Solid Content | 100.0 | % | — |
| Parts Per Hundred Resin/Rubber (PHR) | 50.0 | — | — |
| Mix Viscosity (at 25°C) | 35.0 | cPs | — |